JIS G4305 Grade SUS430J1L annealed

Equivalent material: DIN 1.4664, DIN X2CrCuTi18, JIS SUS430J1LTP, JIS SUS430J1LTB, EN X2CrCuTi18, EN 1.4664

JIS G4305 Grade SUS430J1L annealed general

Property Temperature Value Comment
Density 23.0 °C Density of 7.8 g/cm³ Typical for Steel

JIS G4305 Grade SUS430J1L annealed mechanical

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 190 - 210 GPa Typical for Steel
Elongation A5 23.0 °C Elongation A5 of 22 % -
Hardness, Brinell 23.0 °C Hardness, Brinell of 192 [-] -
Hardness, Rockwell B 23.0 °C Hardness, Rockwell B of 90 [-] -
Hardness, Vickers 23.0 °C Hardness, Vickers of 200 [-] -
Poisson's ratio 23.0 °C Poisson's ratio of 0.3 [-] Typical for Steel
Tensile strength 23.0 °C Tensile strength of 390 MPa -
Yield strength Rp0.2 23.0 °C Yield strength Rp0.2 of 205 MPa -