JIS G4303 Grade SUS316F solution treated
Equivalent material: DIN 1.4401, DIN 316S42, DIN 316S33, DIN X5CrNiMo17-12-2, DIN X 5 CrNiMo 18 10, AFNOR Z7CND17-11-02, BS 316S16, UNI X5CrNiMo1712, SS 2347, UNE F.3543, AISI 316, SAE 316, JIS SUS316, JIS SUS316TKA, JIS SUS316TF, JIS SUS316FB, JIS SUSF316, JIS SUS316TKC, JIS SUS316TP, JIS SUS316TB, JIS SUS316TBS, JIS SUS316TPY, JIS SUS316TPD, JIS SUS316HTP, JIS SUS316HTB, JIS SUS316HTF, EN X5CrNiMo17-12-2, EN 1.4401, ISO A4, GOST 0Cr17Ni12Mo2, GB 08Ch27N13M2, ASTM 316, UNS S31600, IS X04Cr17Ni12Mo2
JIS G4303 Grade SUS316F solution treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4303 Grade SUS316F solution treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4303 Grade SUS316F solution treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4303 Grade SUS316F solution treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 40 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 187 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 90 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 50 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 520 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |