JIS G4108 Grade SNB24-4
Equivalent material: UNI 40NiCrMo7, ASTM 4337, ASTM B24, DIN 1.6565, DIN 40NiCrMo6, BS 817M40, AISI 4340H, AISI E4340H, AISI 4340, SAE 4340H, SAE E4340H, SAE 4340, JIS SNB24, JIS SNCM439, JIS SNB24-1, JIS SNB24-2, JIS SNB24-3, JIS SNB24-5, EN 1.6565, ISO G35CrNiMo6-6, GOST 40Ch2N2MA, GB/T 40CrNiMoA, GB/T A50403, ASTM 4340H, UNS H43400, UNS H43406, UNS G43400
JIS G4108 Grade SNB24-4 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Nickel Chromium Molybdenum Steel |
JIS G4108 Grade SNB24-4 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.3E-5 1/K |
Typical for Nickel Chromium Molybdenum Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Nickel Chromium Molybdenum Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 448 - 670 J/(kg·K) |
Typical for Nickel Chromium Molybdenum Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 34 - 54 W/(m·K) |
Typical for Nickel Chromium Molybdenum Steel |
JIS G4108 Grade SNB24-4 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Nickel Chromium Molybdenum Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 13 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 269 - 363 [-] |
- |
| Impact strength, Charpy notched |
-12.0 °C |
Impact strength, Charpy notched of 40 kJ/m² |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Nickel Chromium Molybdenum Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 45 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 930 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 825 MPa |
- |