JIS G3539 Grade SWCH15A

JIS G3539 Grade SWCH15A

Equivalent material: DIN 1.0234, DIN QSt 38-3, DIN Ma 14, DIN C15C, AFNOR C15C, BS C15C, JIS SWRCH15A, JIS SWRCH15R, JIS SWCH15R, EN C15C, EN 1.0234, ISO CC15A, ISO CC15K, ISO CC15X

JIS G3539 Grade SWCH15A general

Property Temperature Value Comment
Density 23.0 °C Density of 7.8 - 7.9 g/cm³ Typical for Low Carbon Steel

JIS G3539 Grade SWCH15A thermal

Property Temperature Value Comment
Coefficient of thermal expansion 23.0 °C Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K Typical for Low Carbon Steel
Max service temperature - Max service temperature of 500 °C Typical for Carbon Steel
Melting point - Melting point of 1480 - 1526 °C Typical for Low Carbon Steel
Specific heat capacity 23.0 °C Specific heat capacity of 465 J/(kg·K) Typical for Low Carbon Steel
Thermal conductivity 23.0 °C Thermal conductivity of 25 - 93 W/(m·K) Typical for Low Carbon Steel

JIS G3539 Grade SWCH15A magnetic

Property Value Comment
Curie temperature Curie temperature of 770 °C Typical for Low Carbon Steel

JIS G3539 Grade SWCH15A electrical

Property Temperature Value Comment
Electrical resistivity 23.0 °C Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m Typical for Carbon Steel

JIS G3539 Grade SWCH15A mechanical

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 200 - 215 GPa Typical for Low Carbon Steel
Hardness, Rockwell B 23.0 °C Hardness, Rockwell B of 83 - 90 [-] -
Poisson's ratio 23.0 °C Poisson's ratio of 0.29 [-] Typical for Low Carbon Steel
Reduction of area 23.0 °C Reduction of area of 45 - 55 % -
Shear modulus 23.0 °C Shear modulus of 82 GPa Typical for Low Carbon Steel
Tensile strength 23.0 °C Tensile strength of 340 - 590 MPa -