JIS G3204 Grade SFVQ3
Equivalent material: AISI HY100, ASTM L8, ASTM 4N-1, ASTM 4N-2, ASTM 4N-3, DIN 1.6742, DIN 20NiCrMo14-6, EN 20NiCrMo14-6, EN 1.6742, ASTM Grade L8 Class 1
JIS G3204 Grade SFVQ3 general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 - 7.9 g/cm³ | Typical for Nickel Chromium Molybdenum Steel |
JIS G3204 Grade SFVQ3 thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 23.0 °C | Coefficient of thermal expansion of 1E-5 - 1.3E-5 1/K | Typical for Nickel Chromium Molybdenum Steel |
| Melting point | - | Melting point of 1382 - 1529 °C | Typical for Nickel Chromium Molybdenum Steel |
| Specific heat capacity | 23.0 °C | Specific heat capacity of 448 - 670 J/(kg·K) | Typical for Nickel Chromium Molybdenum Steel |
| Thermal conductivity | 23.0 °C | Thermal conductivity of 34 - 54 W/(m·K) | Typical for Nickel Chromium Molybdenum Steel |
JIS G3204 Grade SFVQ3 mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 200 - 215 GPa | Typical for Nickel Chromium Molybdenum Steel |
| Elongation A5 | 23.0 °C | Elongation A5 of 18 % | - |
| Impact strength, Charpy notched | 30.0 °C | Impact strength, Charpy notched of 40 kJ/m² | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.29 [-] | Typical for Nickel Chromium Molybdenum Steel |
| Reduction of area | 23.0 °C | Reduction of area of 48 % | - |
| Tensile strength | 23.0 °C | Tensile strength of 620 - 790 MPa | - |
| Yield strength Rp0.2 | 23.0 °C | Yield strength Rp0.2 of 490 MPa | - |