JIS G3203 Grade SFVAF5A
Equivalent material: GB 1Cr5Mo, GB/T 1Cr5Mo, GB 1Cr5Mo, DIN 12CrMo195, NF Z10CD5-05, BS 625, UNI A16CrMo205KW, UNI B16CrMo205KW, UNI B16CrMo205KG, UNE F.240.B, UNE TU.J, ASTM T5, ASTM P5, ASTM F5, ASTM FP5, ASTM 5, ASTM WP5, JIS SCMV6, JIS SFVAF5B, GOST 20H5ML, GOST 12Ch5VF, NF Z15CD5-05, IS 10Cr5Mo55, UNI 16CrMo205KWKG, UNE AMX18CrMo5, AMS 5502, AMS 5602, ASME 3, ASME 5, ASTM 3, ASTM B5, ASTM 501, JIS STBA25, JIS STPA25, JIS 25, AISI 501, BS 625-520, ASME 502, ASTM 502, MIL 502, AISI 502, DIN 1.7362, DIN 12 CrMo 19 5, DIN X11CrMo5, DIN 12CrMo19-5, DIN X12CrMo5, AFNOR Z10CD5.05, BS 3606-625, BS X11CrMo5, BS X12CrMo5, UNI 16CrMo205, JIS STFA25, JIS SFVAF5C, JIS SFVAF5D, JIS SNB5, EN X12CrMo5, EN X11CrMo5, EN 1.7362, ISO X12CrMo5, ISO X12CrMo5-1, ISO F37, ASTM Grade T5, ASTM Grade B5, ASTM Grade P5, DIN 1.7366, DIN X16CrMo5-1, EN X16CrMo5-1, EN 1.7366
JIS G3203 Grade SFVAF5A general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Molybdenum Steel |
JIS G3203 Grade SFVAF5A thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.4E-5 1/K |
Typical for Chromium Molybdenum Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Molybdenum Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 448 - 502 J/(kg·K) |
Typical for Chromium Molybdenum Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 - 43 W/(m·K) |
Typical for Chromium Molybdenum Steel |
JIS G3203 Grade SFVAF5A mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Chromium Molybdenum Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 18 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Molybdenum Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 40 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 410 - 590 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 245 MPa |
- |