JIS G3128 Grade E460E normalized, controlled rolled
Equivalent material: JIS E460E
JIS G3128 Grade E460E normalized, controlled rolled general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 20.0 °C | Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
JIS G3128 Grade E460E normalized, controlled rolled thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 20.0 °C | Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
| Max service temperature | - | Max service temperature of 500 °C | Typical for Carbon Steel |
| Melting point | - | Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
JIS G3128 Grade E460E normalized, controlled rolled chemical
| Property | Value |
|---|---|
| Aluminium | Aluminium of 0 - 0.02 % |
| Boron | Boron of 0 - 5E-3 % |
| Carbon | Carbon of 0.2 % |
| Chromium | Chromium of 0.7 - 2 % |
| Copper | Copper of 0.7 - 1.5 % |
| Iron | Iron of 90.45 - 99.3 % |
| Manganese | Manganese of 0.7 - 1.7 % |
| Molybdenum | Molybdenum of 0.4 - 1 % |
| Nickel | Nickel of 1 - 2 % |
| Niobium | Niobium of 0 - 0.06 % |
| Nitrogen | Nitrogen of 0 - 0.02 % |
| Phosphorus | Phosphorus of 0.03 % |
| Silicon | Silicon of 0.5 - 0.55 % |
| Sulfur | Sulfur of 0.025 - 0.03 % |
| Titanium | Titanium of 0 - 0.2 % |
| Vanadium | Vanadium of 0 - 0.2 % |
| Zirconium | Zirconium of 0 - 0.15 % |
JIS G3128 Grade E460E normalized, controlled rolled magnetic
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Curie temperature | 20.0 °C | Curie temperature of 770 °C | Typical for Low Carbon Steel |
JIS G3128 Grade E460E normalized, controlled rolled electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
JIS G3128 Grade E460E normalized, controlled rolled mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 20.0 °C | Elastic modulus of 200 - 215 GPa | Typical for Low Carbon Steel |
| Elongation A5 | 20.0 °C | Elongation A5 of 17 % | - |
| Impact strength, Charpy notched | -50.0 °C | Impact strength, Charpy notched of 27 kJ/m² | - |
| Poisson's ratio | 20.0 °C | Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel |
| Shear modulus | 20.0 °C | Shear modulus of 75 - 80 GPa | Typical for Carbon Steel |
| Tensile strength | 20.0 °C | Tensile strength of 510 - 720 MPa | - |
| Yield strength Rp0.2 | 20.0 °C | Yield strength Rp0.2 of 380 - 460 MPa | - |
| impactTransVNotch | -50.0 °C | impactTransVNotch of 16 kJ/m² | - |