JIS C2555 Grade PCYH600 hot-rolled
Equivalent material: DIN 1.0277, JIS PCYC600, EN 600 TG 178, EN 1.0277
JIS C2555 Grade PCYH600 hot-rolled general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
JIS C2555 Grade PCYH600 hot-rolled thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 23.0 °C | Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
| Max service temperature | - | Max service temperature of 500 °C | Typical for Carbon Steel |
| Melting point | - | Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
| Specific heat capacity | 23.0 °C | Specific heat capacity of 465 J/(kg·K) | Typical for Low Carbon Steel |
| Thermal conductivity | 23.0 °C | Thermal conductivity of 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
JIS C2555 Grade PCYH600 hot-rolled magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
JIS C2555 Grade PCYH600 hot-rolled electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Electrical resistivity | 23.0 °C | Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
JIS C2555 Grade PCYH600 hot-rolled mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 200 - 215 GPa | Typical for Low Carbon Steel |
| Elongation A5 | 23.0 °C | Elongation A5 of 11 - 13 % | - |
| Elongation A80 | 23.0 °C | Elongation A80 of 10 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel |
| Shear modulus | 23.0 °C | Shear modulus of 82 GPa | Typical for Low Carbon Steel |
| Tensile strength | 23.0 °C | Tensile strength of 700 MPa | - |
| Yield strength Rp0.2 | 23.0 °C | Yield strength Rp0.2 of 600 MPa | - |