JIS A5530 Grade SKY400 arc welded
Equivalent material: DIN 1.0044, DIN St 44-2, DIN S275JR, AFNOR S275JR, BS 43/25HR, BS 43/25HS, BS 43B, AISI 1021, AISI 1020, SAE 1021, SAE 1020, JIS SS400, JIS STAM390G, JIS SNR400A, JIS SNR400B, JIS SNR490B, JIS SKK400, JIS STKM19C, JIS STKR400, JIS EN275A, JIS E275B, EN S275JR, EN 1.0044, ISO S275JR, ISO EN275A, ISO EN275B, GOST St4ps, GOST St4sp, GB/T Q255A, ASTM Grade 2, ASTM Grade 345 Type 1, ASTM Grade 345 Type 2, ASTM Grade 345 Type 3, UNS G10200, IS EN275A, IS E275B, ASTM Grade B, ASTM Grade 1020, DIN 1.0144, DIN St 44-3 G, DIN St 44-3, DIN S245G, DIN S275J2G3, JIS SM400A, JIS SM400B, JIS SM400C, EN S275J2G3, EN 1.0144, ASTM Grade Ib
JIS A5530 Grade SKY400 arc welded general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
JIS A5530 Grade SKY400 arc welded thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
JIS A5530 Grade SKY400 arc welded magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
JIS A5530 Grade SKY400 arc welded electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS A5530 Grade SKY400 arc welded mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 18 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 400 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 235 MPa |
- |