ISO 683-4 Grade 36SMn14 untreated
ISO 683-4 Grade 36SMn14 untreated introduction
The free-cutting steel 36SMn14, suitable for quenching and tempering, has favorable machining properties. Application for turned parts of mean strength requirements.
Equivalent material: EN 1.0764, ISO 36SMn14, JIS SUM41, SAE 1137, UNS G11370, DIN 1.0764, DIN 36SMn14, AFNOR 36SMn14, BS 36SMn14, BS 216M36, AISI 1137, ASTM Grade 1137, ASTM 1137
ISO 683-4 Grade 36SMn14 untreated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Manganese Steel |
ISO 683-4 Grade 36SMn14 untreated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.33E-5 1/K |
Typical for Manganese Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Manganese Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 510 - 553 J/(kg·K) |
Typical for Manganese Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 16 W/(m·K) |
Typical for Manganese Steel |
ISO 683-4 Grade 36SMn14 untreated chemical
| Property |
Value |
| Carbon |
Carbon of 0.32 - 0.39 % |
| Manganese |
Manganese of 1.3 - 1.7 % |
| Phosphorus |
Phosphorus of 0.06 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.1 - 0.18 % |
ISO 683-4 Grade 36SMn14 untreated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Manganese Steel |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 163 - 225 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Manganese Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 550 - 770 MPa |
- |