ISO 683-3 Grade 16MnCrS5 normalized or normalized formed (+N)
ISO 683-3 Grade 16MnCrS5 normalized or normalized formed (+N) introduction
Steel 16MnCrS5 is suitable for higher dimension parts in vehicle manufacturing and machine engineering, requiring higher core strength and enhanced workability (gear wheels, shafts, steering parts).
Equivalent material: EN 1.7139, IS 16Mn5Cr4(-S), ISO 16MnCrS5, DIN 1.7139, DIN 16MnCrS5, DIN ESP 65
ISO 683-3 Grade 16MnCrS5 normalized or normalized formed (+N) general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.85 g/cm³ |
ISO 683-3 Grade 16MnCrS5 normalized or normalized formed (+N) thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | -100.0 °C | Coefficient of thermal expansion of 1.05E-5 1/K | - |
| - | 20.0 °C | Coefficient of thermal expansion of 1.15E-5 1/K | - |
| - | 100.0 °C | Coefficient of thermal expansion of 1.1E-5 - 1.21E-5 1/K | - |
| - | 200.0 °C | Coefficient of thermal expansion of 1.27E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.32E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.36E-5 1/K | - |
| - | 500.0 °C | Coefficient of thermal expansion of 1.4E-5 1/K | - |
| - | 600.0 °C | Coefficient of thermal expansion of 1.44E-5 1/K | - |
| Melting point | - | Melting point of 1382 - 1529 °C | Typical for Chromium Steel |
| Specific heat capacity | -100.0 °C | Specific heat capacity of 423 J/(kg·K) | - |
| - | 20.0 °C | Specific heat capacity of 460 - 461 J/(kg·K) | - |
| - | 100.0 °C | Specific heat capacity of 479 J/(kg·K) | - |
| - | 200.0 °C | Specific heat capacity of 499 J/(kg·K) | - |
| - | 300.0 °C | Specific heat capacity of 517 J/(kg·K) | - |
| - | 400.0 °C | Specific heat capacity of 536 J/(kg·K) | - |
| - | 500.0 °C | Specific heat capacity of 558 J/(kg·K) | - |
| - | 600.0 °C | Specific heat capacity of 587 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 42 - 45.9 W/(m·K) | - |
| - | 100.0 °C | Thermal conductivity of 39.8 - 46.4 W/(m·K) | - |
| - | 200.0 °C | Thermal conductivity of 37.7 - 45.6 W/(m·K) | - |
| - | 300.0 °C | Thermal conductivity of 43.5 W/(m·K) | - |
| - | 400.0 °C | Thermal conductivity of 40.9 W/(m·K) | - |
| - | 500.0 °C | Thermal conductivity of 38.2 W/(m·K) | - |
| - | 600.0 °C | Thermal conductivity of 35.5 W/(m·K) | - |
| Thermal diffusivity | 20.0 °C | Thermal diffusivity of 12.7 mm²/s | - |
| - | 100.0 °C | Thermal diffusivity of 12 mm²/s | - |
| - | 200.0 °C | Thermal diffusivity of 11 mm²/s | - |
| - | 300.0 °C | Thermal diffusivity of 9.9 mm²/s | - |
| - | 400.0 °C | Thermal diffusivity of 8.7 mm²/s | - |
| - | 500.0 °C | Thermal diffusivity of 7.3 mm²/s | - |
| - | 600.0 °C | Thermal diffusivity of 6 mm²/s | - |
ISO 683-3 Grade 16MnCrS5 normalized or normalized formed (+N) chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.14 - 0.19 % |
| Chromium | Chromium of 0.8 - 1.1 % |
| Copper | Copper of 0.4 % |
| Manganese | Manganese of 1 - 1.3 % |
| Phosphorus | Phosphorus of 0.03 % |
| Silicon | Silicon of 0.15 - 0.4 % |
| Sulfur | Sulfur of 0.02 - 0.04 % |
ISO 683-3 Grade 16MnCrS5 normalized or normalized formed (+N) electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 1.6E-7 - 2.27E-7 Ω·m |
| - | 100.0 °C | Electrical resistivity of 2.76E-7 Ω·m |
| - | 200.0 °C | Electrical resistivity of 3.46E-7 Ω·m |
| - | 300.0 °C | Electrical resistivity of 4.31E-7 Ω·m |
| - | 400.0 °C | Electrical resistivity of 5.32E-7 Ω·m |
| - | 500.0 °C | Electrical resistivity of 6.48E-7 Ω·m |
| - | 600.0 °C | Electrical resistivity of 7.81E-7 Ω·m |
ISO 683-3 Grade 16MnCrS5 normalized or normalized formed (+N) mechanical
| Property | Temperature | Value |
|---|---|---|
| Elastic modulus | -100.0 °C | Elastic modulus of 217 GPa |
| - | 20.0 °C | Elastic modulus of 210 - 212 GPa |
| - | 100.0 °C | Elastic modulus of 207 GPa |
| - | 200.0 °C | Elastic modulus of 188 - 199 GPa |
| - | 300.0 °C | Elastic modulus of 192 GPa |
| - | 400.0 °C | Elastic modulus of 184 GPa |
| - | 500.0 °C | Elastic modulus of 175 GPa |
| - | 600.0 °C | Elastic modulus of 164 GPa |
| Poisson's ratio | 20.0 °C | Poisson's ratio of 0.28 [-] |
| - | 25.0 °C | Poisson's ratio of 0.26 - 0.29 [-] |
| Shear modulus | 20.0 °C | Shear modulus of 81 GPa |
Our skilled craftsmen work tirelessly to produce steel products of the highest quality and precision.
-- Our promise
Similar or equivalent steel materials
- EN 10277-4 Grade 16MnCrS5 soft annealed and peeled (+A+SH)
- EN 10277-4 Grade 16MnCrS5 soft annealed and cold drawn (+A+C)
- EN 10277-4 Grade 16MnCrS5 treated to ferritic-pearlite structure and turned (+FP+SH)
- EN 10277-4 Grade 16MnCrS5 treated to ferritic-pearlite structure and hardness range and cold-drawn (+FP+C)
- DIN 1652-3 Grade 16MnCrS5 treated to ferritic-pearlite structure and cold-drawn
- DIN 1652-3 Grade 16MnCrS5 cold drawn
- DIN 1652-3 Grade 16MnCrS5 cold-drawn or peeled and treated to ferrite-pearlite structure
- DIN 1652-3 Grade 16MnCrS5 cold drawn or turned and soft annealed
- DIN 17210 Grade 16MnCrS5 soft annealed (+A)