ISO 683-17 Grade 16CrNiMo6 annealed to achieve spheroidized carbides, cold worked (+AC+C)
ISO 683-17 Grade 16CrNiMo6 annealed to achieve spheroidized carbides, cold worked (+AC+C) introduction
16 CrNiMo 6 is a case hardening steel for anti-friction bearings. In the Jominy test it reaches surface hardnesses of approximately 48 HRC. It is used for anti-friction bearing parts that are subjected to medium stress.
Equivalent material: DIN 18NiCrMo7-6
ISO 683-17 Grade 16CrNiMo6 annealed to achieve spheroidized carbides, cold worked (+AC+C) general
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | -100.0 °C | Electrical resistivity of 2.14E-7 Ω·m |
| - | 0.0 °C | Electrical resistivity of 2.66E-7 Ω·m |
| - | 20.0 °C | Electrical resistivity of 2.77E-7 Ω·m |
| - | 100.0 °C | Electrical resistivity of 3.26E-7 Ω·m |
| - | 200.0 °C | Electrical resistivity of 3.94E-7 Ω·m |
| - | 300.0 °C | Electrical resistivity of 4.74E-7 Ω·m |
| - | 400.0 °C | Electrical resistivity of 5.66E-7 Ω·m |
| - | 500.0 °C | Electrical resistivity of 6.73E-7 Ω·m |
| - | 600.0 °C | Electrical resistivity of 7.96E-7 Ω·m |
ISO 683-17 Grade 16CrNiMo6 annealed to achieve spheroidized carbides, cold worked (+AC+C) thermal
| Property | Temperature | Value |
|---|---|---|
| Elastic modulus | -100.0 °C | Elastic modulus of 217 GPa |
| - | 0.0 °C | Elastic modulus of 213 GPa |
| - | 20.0 °C | Elastic modulus of 212 GPa |
| - | 100.0 °C | Elastic modulus of 207 GPa |
| - | 200.0 °C | Elastic modulus of 199 GPa |
| - | 300.0 °C | Elastic modulus of 192 GPa |
| - | 400.0 °C | Elastic modulus of 184 GPa |
| - | 500.0 °C | Elastic modulus of 175 GPa |
| - | 600.0 °C | Elastic modulus of 164 GPa |
| Hardness, Brinell | 20.0 °C | Hardness, Brinell of 229 [-] |
ISO 683-17 Grade 16CrNiMo6 annealed to achieve spheroidized carbides, cold worked (+AC+C) chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.15 - 0.2 % |
| Chromium | Chromium of 1.5 - 1.8 % |
| Copper | Copper of 0.3 % |
| Manganese | Manganese of 0.4 - 0.6 % |
| Molybdenum | Molybdenum of 0.25 - 0.35 % |
| Nickel | Nickel of 1.4 - 1.7 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 0.4 % |
| Sulfur | Sulfur of 0.035 % |
ISO 683-17 Grade 16CrNiMo6 annealed to achieve spheroidized carbides, cold worked (+AC+C) electrical
| Property | Temperature | Value |
|---|---|---|
| Coefficient of thermal expansion | -100.0 °C | Coefficient of thermal expansion of 1.05E-5 1/K |
| - | 0.0 °C | Coefficient of thermal expansion of 1.14E-5 1/K |
| - | 20.0 °C | Coefficient of thermal expansion of 1.15E-5 1/K |
| - | 100.0 °C | Coefficient of thermal expansion of 1.21E-5 1/K |
| - | 200.0 °C | Coefficient of thermal expansion of 1.27E-5 1/K |
| - | 300.0 °C | Coefficient of thermal expansion of 1.32E-5 1/K |
| - | 400.0 °C | Coefficient of thermal expansion of 1.36E-5 1/K |
| - | 500.0 °C | Coefficient of thermal expansion of 1.4E-5 1/K |
| - | 600.0 °C | Coefficient of thermal expansion of 1.44E-5 1/K |
| Specific heat capacity | -100.0 °C | Specific heat capacity of 423 J/(kg·K) |
| - | 0.0 °C | Specific heat capacity of 456 J/(kg·K) |
| - | 20.0 °C | Specific heat capacity of 461 J/(kg·K) |
| - | 100.0 °C | Specific heat capacity of 479 J/(kg·K) |
| - | 200.0 °C | Specific heat capacity of 499 J/(kg·K) |
| - | 300.0 °C | Specific heat capacity of 517 J/(kg·K) |
| - | 400.0 °C | Specific heat capacity of 536 J/(kg·K) |
| - | 500.0 °C | Specific heat capacity of 558 J/(kg·K) |
| - | 600.0 °C | Specific heat capacity of 587 J/(kg·K) |
| Thermal conductivity | -100.0 °C | Thermal conductivity of 31.9 W/(m·K) |
| - | 0.0 °C | Thermal conductivity of 36.9 W/(m·K) |
| - | 20.0 °C | Thermal conductivity of 37.6 W/(m·K) |
| - | 100.0 °C | Thermal conductivity of 39.3 W/(m·K) |
| - | 200.0 °C | Thermal conductivity of 40.1 W/(m·K) |
| - | 300.0 °C | Thermal conductivity of 39.6 W/(m·K) |
| - | 400.0 °C | Thermal conductivity of 38.4 W/(m·K) |
| - | 500.0 °C | Thermal conductivity of 36.7 W/(m·K) |
| - | 600.0 °C | Thermal conductivity of 34.8 W/(m·K) |
| Thermal diffusivity | -100.0 °C | Thermal diffusivity of 10900 mm²/s |
| - | 0.0 °C | Thermal diffusivity of 10400 mm²/s |
| - | 20.0 °C | Thermal diffusivity of 10400 mm²/s |
| - | 100.0 °C | Thermal diffusivity of 10100 mm²/s |
| - | 200.0 °C | Thermal diffusivity of 9700 mm²/s |
| - | 300.0 °C | Thermal diffusivity of 9000 mm²/s |
| - | 400.0 °C | Thermal diffusivity of 8100 mm²/s |
| - | 500.0 °C | Thermal diffusivity of 7100 mm²/s |
| - | 600.0 °C | Thermal diffusivity of 5900 mm²/s |
ISO 683-17 Grade 16CrNiMo6 annealed to achieve spheroidized carbides, cold worked (+AC+C) mechanical
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.84 - 7.85 g/cm³ |
Explore limitless design possibilities with our versatile range of steel products.
-- Our promise
Similar or equivalent steel materials
- ISO 683-17 Grade 16CrNiMo6 annealed to achieve spheroidized carbides (+AC)
- ISO 683-17 Grade 16CrNiMo6 annealed to achieve spheroidized carbides and ground
- ISO 683-17 Grade 16CrNiMo6 treated to ferritic-pearlite structure
- ISO 683-17 Grade 16CrNiMo6 treatment to hardness range (+TH)
- DIN 17230 Grade 16CrNiMo6 annealed to achieve spheroidized carbides (+AC)
- ISO 683-17 Grade 16CrNiMo6 annealed to achieve spheroidized carbides and turned