ISO 4957 Grade X19NiCrMo4 case hardened, edge-zone
ISO 4957 Grade X19NiCrMo4 case hardened, edge-zone introduction
case-hardened steel, hardenable on air, low distortion, surface application hardness 58-60 HRC
for plastic dies
ISO 4957 Grade X19NiCrMo4 case hardened, edge-zone general
Property |
Temperature |
Value |
Density |
20.0 °C |
Density of 7.86 g/cm³ |
ISO 4957 Grade X19NiCrMo4 case hardened, edge-zone thermal
Property |
Temperature |
Value |
Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.15E-5 1/K |
- |
200.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
300.0 °C |
Coefficient of thermal expansion of 1.24E-5 1/K |
- |
400.0 °C |
Coefficient of thermal expansion of 1.28E-5 1/K |
- |
500.0 °C |
Coefficient of thermal expansion of 1.31E-5 1/K |
- |
600.0 °C |
Coefficient of thermal expansion of 1.35E-5 1/K |
Specific heat capacity |
20.0 °C |
Specific heat capacity of 464 J/(kg·K) |
- |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
200.0 °C |
Specific heat capacity of 496 J/(kg·K) |
- |
300.0 °C |
Specific heat capacity of 513 J/(kg·K) |
- |
400.0 °C |
Specific heat capacity of 532 J/(kg·K) |
Thermal conductivity |
20.0 °C |
Thermal conductivity of 32.9 W/(m·K) |
- |
100.0 °C |
Thermal conductivity of 34.2 W/(m·K) |
- |
200.0 °C |
Thermal conductivity of 34.8 W/(m·K) |
- |
300.0 °C |
Thermal conductivity of 34.4 W/(m·K) |
- |
400.0 °C |
Thermal conductivity of 33.3 W/(m·K) |
Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 9 mm²/s |
- |
100.0 °C |
Thermal diffusivity of 8.8 mm²/s |
- |
200.0 °C |
Thermal diffusivity of 8.5 mm²/s |
- |
300.0 °C |
Thermal diffusivity of 7.8 mm²/s |
- |
400.0 °C |
Thermal diffusivity of 7.1 mm²/s |
ISO 4957 Grade X19NiCrMo4 case hardened, edge-zone chemical
Property |
Value |
Carbon |
Carbon of 0.16 - 0.22 % |
Chromium |
Chromium of 1.1 - 1.4 % |
Manganese |
Manganese of 0.15 - 0.45 % |
Molybdenum |
Molybdenum of 0.15 - 0.25 % |
Nickel |
Nickel of 3.8 - 4.3 % |
Phosphorus |
Phosphorus of 0.03 % |
Silicon |
Silicon of 0.1 - 0.4 % |
Sulfur |
Sulfur of 0.03 % |
Tungsten |
Tungsten of 0.3 - 0.5 % |
ISO 4957 Grade X19NiCrMo4 case hardened, edge-zone electrical
Property |
Temperature |
Value |
Electrical resistivity |
20.0 °C |
Electrical resistivity of 3.17E-7 Ω·m |
- |
100.0 °C |
Electrical resistivity of 3.74E-7 Ω·m |
- |
200.0 °C |
Electrical resistivity of 4.54E-7 Ω·m |
- |
300.0 °C |
Electrical resistivity of 5.46E-7 Ω·m |
- |
400.0 °C |
Electrical resistivity of 6.53E-7 Ω·m |
ISO 4957 Grade X19NiCrMo4 case hardened, edge-zone mechanical
Property |
Temperature |
Value |
Elastic modulus |
20.0 °C |
Elastic modulus of 207 GPa |
- |
100.0 °C |
Elastic modulus of 203 GPa |
- |
200.0 °C |
Elastic modulus of 197 GPa |
- |
300.0 °C |
Elastic modulus of 189 GPa |
- |
400.0 °C |
Elastic modulus of 181 GPa |
- |
500.0 °C |
Elastic modulus of 172 GPa |