ISO 4957 Grade 62SiMnCr4

ISO 4957 Grade 62SiMnCr4

ISO 4957 Grade 62SiMnCr4 introduction

Properties:
- tough, dimension stable, save for distortion, wear resistant
- for air and oil hardening
Application:
- for pressure loaded tools
- draw and bending tools, dies, thread rolls, forming rolls for profile and tube manufacturing form strip
- for roll and blade shear knifes for sheet thickness up to 4mm

Equivalent material: DIN 1.2101, EN 62SiMnCr4, EN 1.2101

ISO 4957 Grade 62SiMnCr4 general

Property Temperature Value
Density 20.0 °C Density of 7.8 g/cm³

ISO 4957 Grade 62SiMnCr4 thermal

Property Temperature Value Comment
Coefficient of thermal expansion -100.0 °C Coefficient of thermal expansion of 1.08E-5 1/K -
- 20.0 °C Coefficient of thermal expansion of 1.19E-5 1/K -
- 100.0 °C Coefficient of thermal expansion of 1.25E-5 1/K -
- 200.0 °C Coefficient of thermal expansion of 1.3E-5 1/K -
- 300.0 °C Coefficient of thermal expansion of 1.36E-5 1/K -
- 400.0 °C Coefficient of thermal expansion of 1.41E-5 1/K -
- 500.0 °C Coefficient of thermal expansion of 1.45E-5 1/K -
- 600.0 °C Coefficient of thermal expansion of 1.49E-5 1/K -
Melting point - Melting point of 1370 - 1425 °C Typical for Tool And Machining Steel
Specific heat capacity -100.0 °C Specific heat capacity of 423 J/(kg·K) -
- 20.0 °C Specific heat capacity of 461 J/(kg·K) -
- 100.0 °C Specific heat capacity of 479 J/(kg·K) -
- 200.0 °C Specific heat capacity of 499 J/(kg·K) -
- 300.0 °C Specific heat capacity of 517 J/(kg·K) -
- 400.0 °C Specific heat capacity of 536 J/(kg·K) -
- 500.0 °C Specific heat capacity of 558 J/(kg·K) -
- 600.0 °C Specific heat capacity of 587 J/(kg·K) -
Thermal conductivity 20.0 °C Thermal conductivity of 41.7 W/(m·K) -
- 100.0 °C Thermal conductivity of 43.4 W/(m·K) -
- 200.0 °C Thermal conductivity of 43.2 W/(m·K) -
- 300.0 °C Thermal conductivity of 41.4 W/(m·K) -
- 400.0 °C Thermal conductivity of 39.1 W/(m·K) -
- 500.0 °C Thermal conductivity of 36.7 W/(m·K) -
- 600.0 °C Thermal conductivity of 34.1 W/(m·K) -
Thermal diffusivity 20.0 °C Thermal diffusivity of 11.6 mm²/s -
- 100.0 °C Thermal diffusivity of 11.3 mm²/s -
- 200.0 °C Thermal diffusivity of 10.5 mm²/s -
- 300.0 °C Thermal diffusivity of 9.5 mm²/s -
- 400.0 °C Thermal diffusivity of 8.3 mm²/s -
- 500.0 °C Thermal diffusivity of 7.1 mm²/s -
- 600.0 °C Thermal diffusivity of 5.8 mm²/s -

ISO 4957 Grade 62SiMnCr4 chemical

Property Value
Carbon Carbon of 0.66 %
Chromium Chromium of 0.4 - 0.7 %
Manganese Manganese of 0.9 - 1.2 %
Phosphorus Phosphorus of 0.03 %
Silicon Silicon of 0.9 - 1.2 %
Sulfur Sulfur of 0.03 %

ISO 4957 Grade 62SiMnCr4 electrical

Property Temperature Value
Electrical resistivity 20.0 °C Electrical resistivity of 2.5E-7 Ω·m
- 100.0 °C Electrical resistivity of 2.95E-7 Ω·m
- 200.0 °C Electrical resistivity of 3.65E-7 Ω·m
- 300.0 °C Electrical resistivity of 4.53E-7 Ω·m
- 400.0 °C Electrical resistivity of 5.56E-7 Ω·m
- 500.0 °C Electrical resistivity of 6.74E-7 Ω·m
- 600.0 °C Electrical resistivity of 8.13E-7 Ω·m

ISO 4957 Grade 62SiMnCr4 mechanical

Property Temperature Value Comment
Elastic modulus -100.0 °C Elastic modulus of 217 GPa -
- 20.0 °C Elastic modulus of 212 GPa -
- 100.0 °C Elastic modulus of 207 GPa -
- 200.0 °C Elastic modulus of 199 GPa -
- 300.0 °C Elastic modulus of 192 GPa -
- 400.0 °C Elastic modulus of 184 GPa -
- 500.0 °C Elastic modulus of 175 GPa -
- 600.0 °C Elastic modulus of 164 GPa -
Poisson's ratio 23.0 °C Poisson's ratio of 0.3 [-] Typical for Tool And Machining Steel
Shear modulus 23.0 °C Shear modulus of 79 GPa Typical for Tool And Machining Steel