ISO 16120-4 Grade C15D2
ISO 16120-4 Grade C15D2 introduction
Non-alloy steel wire rod for drawing and/or cold rolling with specific requirements for special applications (e.g. application for springs, steel wire).
Equivalent material: GB C15D2, ISO C15D2, DIN 1.1126, DIN C15D2, AFNOR C15D2, BS C15D2, EN 1.1126, GB/T C15D2
ISO 16120-4 Grade C15D2 general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
ISO 16120-4 Grade C15D2 thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 23.0 °C | Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
| Max service temperature | - | Max service temperature of 500 °C | Typical for Carbon Steel |
| Melting point | - | Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
| Specific heat capacity | 23.0 °C | Specific heat capacity of 465 J/(kg·K) | Typical for Low Carbon Steel |
| Thermal conductivity | 23.0 °C | Thermal conductivity of 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
ISO 16120-4 Grade C15D2 chemical
| Property | Value |
|---|---|
| Aluminium | Aluminium of 0.01 % |
| Carbon | Carbon of 0.13 - 0.17 % |
| Chromium | Chromium of 0.1 % |
| Copper | Copper of 0.15 % |
| Manganese | Manganese of 0.3 - 0.5 % |
| Molybdenum | Molybdenum of 0.05 % |
| Nickel | Nickel of 0.1 % |
| Nitrogen | Nitrogen of 7E-3 % |
| Phosphorus | Phosphorus of 0.02 % |
| Silicon | Silicon of 0.3 % |
| Sulfur | Sulfur of 0.025 % |
ISO 16120-4 Grade C15D2 magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
ISO 16120-4 Grade C15D2 electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Electrical resistivity | 23.0 °C | Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
ISO 16120-4 Grade C15D2 mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 200 - 215 GPa | Typical for Low Carbon Steel |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel |
| Shear modulus | 23.0 °C | Shear modulus of 82 GPa | Typical for Low Carbon Steel |