EN 10292 Grade HX220PD +Z, +ZF, +ZA, +AZ, +AS,hot rolled or cold rolled, hot dip coated
EN 10292 Grade HX220PD +Z, +ZF, +ZA, +AZ, +AS,hot rolled or cold rolled, hot dip coated introduction
The steel HX220PD (X=roll condition, P=phosphorus alloyed, D=hot-dip coatable) is producible with the following coatings:
- HX220PD+Z (plating Zn) with coating weights (double-sided) of 100, 140, 200, 225 and 275 g/m² (100 g approximate 7,1 µm per side)
- HX220PD+ZF (plating Zn-Fe) with coating weights (double-sided) of 100 and 120 g/m² (100 g approximate 7,1 µm per side)
- HX220PD+ZA (plating Zn-Al) with coating weights (double-sided) of 095, 130, 185, 200 and 255 g/m² (95 g approximate 7,2 µm per side)
- HX220PD+AZ (plating Al-Zn) with coating weights (double-sided) of 100, 150 and 185 g/m² (100 g approximate 13,3 µm per side)
- HX220PD+AS (plating Al-Si) with coating weights (double-sided) of 060 and 080 g/m² (100 g approximate 17 µm per side)
The hot dip galvanizing refined flat products are available by arrangement on ordering with different coating weights (also per side).
Following surface protection types can be delivered: chemical passivated, oiled, chemical passivated and oiled, sealed, phosphated, phosphated and oiled.
Mechanical properties are warranted for a period of 3 months for Bake-hardening steels and for a period of 6 months after provision of the products for all other sorts. The same terms are valid for freedom from stretcher strains (surface type B and C).
It is suitable for usual welding methods. For higher coating weights on welding are where approppriate necessary special measures.
Furthermore suitability for joining by sticking as well as for application of organic coatings.
Application:
household appliances industry, construction trade, electrical industry, furniture industry, car industry.
Equivalent material: DIN 1.0358, EN 1.0358
EN 10292 Grade HX220PD +Z, +ZF, +ZA, +AZ, +AS,hot rolled or cold rolled, hot dip coated general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10292 Grade HX220PD +Z, +ZF, +ZA, +AZ, +AS,hot rolled or cold rolled, hot dip coated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
EN 10292 Grade HX220PD +Z, +ZF, +ZA, +AZ, +AS,hot rolled or cold rolled, hot dip coated chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Carbon |
Carbon of 0.06 % |
| Manganese |
Manganese of 0.7 % |
| Phosphorus |
Phosphorus of 0.08 % |
| Silicon |
Silicon of 0.5 % |
| Sulfur |
Sulfur of 0.025 % |
EN 10292 Grade HX220PD +Z, +ZF, +ZA, +AZ, +AS,hot rolled or cold rolled, hot dip coated electrical
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10292 Grade HX220PD +Z, +ZF, +ZA, +AZ, +AS,hot rolled or cold rolled, hot dip coated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A80, transverse |
20.0 °C |
Elongation A80, transverse of 32 % |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 340 - 400 MPa |
- |
| Yield strength Rp0.2, transverse |
20.0 °C |
Yield strength Rp0.2, transverse of 220 - 280 MPa |
- |
We are committed to your success, providing reliable steel solutions that exceed expectations.