EN 10277-2 Grade ZSt44-3 turned
EN 10277-2 Grade ZSt44-3 turned introduction
ZSt 44-3 as bright drawn fine grained grade is used for dynamic loaded welded constructions up to a temperature of -20 °C.
Equivalent material: DIN 1.0153, EN 1.0153
EN 10277-2 Grade ZSt44-3 turned general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.85 g/cm³ |
EN 10277-2 Grade ZSt44-3 turned thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | -100.0 °C | Coefficient of thermal expansion of 1.08E-5 1/K | - |
| - | 20.0 °C | Coefficient of thermal expansion of 1.19E-5 1/K | - |
| - | 100.0 °C | Coefficient of thermal expansion of 1.25E-5 1/K | - |
| - | 200.0 °C | Coefficient of thermal expansion of 1.3E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.36E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.41E-5 1/K | - |
| - | 500.0 °C | Coefficient of thermal expansion of 1.45E-5 1/K | - |
| - | 600.0 °C | Coefficient of thermal expansion of 1.49E-5 1/K | - |
| Max service temperature | - | Max service temperature of 500 °C | Typical for Carbon Steel |
| Max service temperature, long | - | Max service temperature, long of -20 - 0 °C | - |
| Melting point | - | Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
| Specific heat capacity | -100.0 °C | Specific heat capacity of 423 J/(kg·K) | - |
| - | 20.0 °C | Specific heat capacity of 461 J/(kg·K) | - |
| - | 100.0 °C | Specific heat capacity of 479 J/(kg·K) | - |
| - | 200.0 °C | Specific heat capacity of 499 J/(kg·K) | - |
| - | 300.0 °C | Specific heat capacity of 517 J/(kg·K) | - |
| - | 400.0 °C | Specific heat capacity of 536 J/(kg·K) | - |
| - | 500.0 °C | Specific heat capacity of 558 J/(kg·K) | - |
| - | 600.0 °C | Specific heat capacity of 587 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 53.4 W/(m·K) | - |
| - | 100.0 °C | Thermal conductivity of 52.9 W/(m·K) | - |
| - | 200.0 °C | Thermal conductivity of 50.3 W/(m·K) | - |
| - | 300.0 °C | Thermal conductivity of 46.7 W/(m·K) | - |
| - | 400.0 °C | Thermal conductivity of 43.3 W/(m·K) | - |
| - | 500.0 °C | Thermal conductivity of 39.8 W/(m·K) | - |
| - | 600.0 °C | Thermal conductivity of 36.7 W/(m·K) | - |
| Thermal diffusivity | 20.0 °C | Thermal diffusivity of 14.8 mm²/s | - |
| - | 100.0 °C | Thermal diffusivity of 13.6 mm²/s | - |
| - | 200.0 °C | Thermal diffusivity of 12.1 mm²/s | - |
| - | 300.0 °C | Thermal diffusivity of 10.6 mm²/s | - |
| - | 400.0 °C | Thermal diffusivity of 9.2 mm²/s | - |
| - | 500.0 °C | Thermal diffusivity of 7.7 mm²/s | - |
| - | 600.0 °C | Thermal diffusivity of 6.2 mm²/s | - |
EN 10277-2 Grade ZSt44-3 turned chemical
| Property | Value |
|---|---|
| Aluminium | Aluminium of 0.02 % |
| Carbon | Carbon of 0.2 % |
| Phosphorus | Phosphorus of 0.04 % |
| Sulfur | Sulfur of 0.04 % |
EN 10277-2 Grade ZSt44-3 turned magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
EN 10277-2 Grade ZSt44-3 turned electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 1.95E-7 Ω·m |
| - | 100.0 °C | Electrical resistivity of 2.42E-7 Ω·m |
| - | 200.0 °C | Electrical resistivity of 3.14E-7 Ω·m |
| - | 300.0 °C | Electrical resistivity of 4.02E-7 Ω·m |
| - | 400.0 °C | Electrical resistivity of 5.02E-7 Ω·m |
| - | 500.0 °C | Electrical resistivity of 6.21E-7 Ω·m |
| - | 600.0 °C | Electrical resistivity of 7.55E-7 Ω·m |
EN 10277-2 Grade ZSt44-3 turned mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | -100.0 °C | Elastic modulus of 217 GPa | - |
| - | 20.0 °C | Elastic modulus of 212 GPa | - |
| - | 100.0 °C | Elastic modulus of 207 GPa | - |
| - | 200.0 °C | Elastic modulus of 199 GPa | - |
| - | 300.0 °C | Elastic modulus of 192 GPa | - |
| - | 400.0 °C | Elastic modulus of 184 GPa | - |
| - | 500.0 °C | Elastic modulus of 175 GPa | - |
| - | 600.0 °C | Elastic modulus of 164 GPa | - |
| Elongation | 20.0 °C | Elongation of 18 - 20 % | - |
| Poisson's ratio | 20.0 °C | Poisson's ratio of 0.28 [-] | - |
| Shear modulus | 23.0 °C | Shear modulus of 82 GPa | Typical for Low Carbon Steel |
| Tensile strength | 20.0 °C | Tensile strength of 410 - 500 MPa | - |
| Yield strength | 20.0 °C | Yield strength of 245 - 265 MPa | - |