EN 10273 Grade P500QH quenched and tempered (+QT)
EN 10273 Grade P500QH quenched and tempered (+QT) introduction
The steel P500QH is a high temperature steel suitable for welding.
Application: use in pressure vessel engineering.
Equivalent material: DIN BEStE550TM, DIN 1.8874, EN 1.8874
EN 10273 Grade P500QH quenched and tempered (+QT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
EN 10273 Grade P500QH quenched and tempered (+QT) chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.018 % |
| Boron |
Boron of 5E-3 % |
| Carbon |
Carbon of 0.18 % |
| Chromium |
Chromium of 1 % |
| Copper |
Copper of 0.3 % |
| Manganese |
Manganese of 1.7 % |
| Molybdenum |
Molybdenum of 0.7 % |
| Nickel |
Nickel of 1.5 % |
| Niobium |
Niobium of 0.05 % |
| Nitrogen |
Nitrogen of 0.02 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.6 % |
| Sulfur |
Sulfur of 0.01 - 0.015 % |
| Titanium |
Titanium of 0.05 % |
| Vanadium |
Vanadium of 0.08 % |
| Zirconium |
Zirconium of 0.15 % |
EN 10273 Grade P500QH quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
Typical for Steel |
| Elongation |
20.0 °C |
Elongation of 17 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 540 - 770 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 440 - 500 MPa |
- |
| Yield strength Rp0.2 |
50.0 °C |
Yield strength Rp0.2 of 430 - 490 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 410 - 470 MPa |
- |
| - |
150.0 °C |
Yield strength Rp0.2 of 390 - 450 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 360 - 420 MPa |
- |
| - |
250.0 °C |
Yield strength Rp0.2 of 340 - 400 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 320 - 380 MPa |
- |