EN 10270-2 Grade VDC oil quenched and tempered
EN 10270-2 Grade VDC oil quenched and tempered introduction
The round, oil hardened and tempered carbon steel wire VDC with high fatigue strength and low tensile strength is used mainly for torsion loaded springs (tension and compression springs) mostly at room temperature.
It will be delivered in rings, in coils or as bars and, if not otherwise arranged, thin oiled.
Der runde, ölschlußvergütete Ventilfederdraht der Sorte VDC aus unlegiertem Stahl mit hoher Dauerfestigkeit und niedriger Zugfestigkeit wird vorzugsweise verwendet für torsionsbeanspruchte Federn (Zug- und Druckfedern) im allgemeinen bei Raumtemperatur.
Der Draht wird in Ringen, auf Spulen oder in Stäben und, wenn nicht anders vereinbart, im leicht geölten Zustand geliefert.
Equivalent material: AS 1472, IS VDC, ISO VDC, DIN VD(1.1250), DIN VD C, AFNOR VDC, BS VDC
EN 10270-2 Grade VDC oil quenched and tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for High Carbon Steel |
EN 10270-2 Grade VDC oil quenched and tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
Typical for High Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 486 J/(kg·K) |
Typical for High Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 W/(m·K) |
Typical for High Carbon Steel |
EN 10270-2 Grade VDC oil quenched and tempered chemical
| Property |
Value |
| Carbon |
Carbon of 0.6 - 0.75 % |
| Copper |
Copper of 0.06 % |
| Manganese |
Manganese of 0.5 - 1 % |
| Phosphorus |
Phosphorus of 0.02 % |
| Silicon |
Silicon of 0.15 - 0.3 % |
| Sulfur |
Sulfur of 0.02 % |
EN 10270-2 Grade VDC oil quenched and tempered electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10270-2 Grade VDC oil quenched and tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 206 GPa |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 38 - 50 % |
- |
| Shear modulus |
20.0 °C |
Shear modulus of 79.5 - 81.5 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 1390 - 2000 MPa |
- |