EN 10270-2 Grade FDCrV oil quenched and tempered
EN 10270-2 Grade FDCrV oil quenched and tempered introduction
The round, oil hardened and tempered alloy steel wire FDCrV for static loading and medium tensile strength is used mainly for torsion loaded springs (tension and compression springs).
It will be delivered in rings, in coils or as bars and, if not otherwise arranged, thin oiled.
Equivalent material: IS FDCrV-B, ISO FDCrV, DIN FD CrV, AFNOR FDCrV, BS FDCrV
EN 10270-2 Grade FDCrV oil quenched and tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Vanadium Steel |
EN 10270-2 Grade FDCrV oil quenched and tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
Typical for Chromium Vanadium Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Vanadium Steel |
EN 10270-2 Grade FDCrV oil quenched and tempered chemical
| Property |
Value |
| Carbon |
Carbon of 0.62 - 0.72 % |
| Chromium |
Chromium of 0.4 - 0.6 % |
| Copper |
Copper of 0.12 % |
| Manganese |
Manganese of 0.5 - 0.9 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.3 % |
| Sulfur |
Sulfur of 0.025 % |
| Vanadium |
Vanadium of 0.15 - 0.25 % |
EN 10270-2 Grade FDCrV oil quenched and tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 206 GPa |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Vanadium Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 30 - 45 % |
- |
| Shear modulus |
20.0 °C |
Shear modulus of 79.5 - 81.5 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 1400 - 2200 MPa |
- |