EN 10269 Grade 35B2 quenched and tempered (+QT)
EN 10269 Grade 35B2 quenched and tempered (+QT) introduction
Application for mounting elements at increased temperatures.
Equivalent material: UNE F.1294-35B3DF, DIN 35B2, DIN 1.5511, DIN YB, AFNOR 38B3, JIS SWRCHB234, JIS SWRCHB237, JIS SWCHB237, EN 1.5511
EN 10269 Grade 35B2 quenched and tempered (+QT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.82 - 7.85 g/cm³ |
EN 10269 Grade 35B2 quenched and tempered (+QT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.11E-5 - 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.21E-5 - 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.29E-5 - 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1380 - 1514 °C |
Typical for Medium Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 48 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 48.9 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 47.5 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 44.7 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 41.6 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 38.6 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 35.5 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 13.3 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 12.6 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 11.5 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 10.2 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.9 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.5 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 6 mm²/s |
- |
EN 10269 Grade 35B2 quenched and tempered (+QT) chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Boron |
Boron of 8E-4 - 5E-3 % |
| Carbon |
Carbon of 0.32 - 0.4 % |
| Manganese |
Manganese of 0.5 - 0.8 % |
| Phosphorus |
Phosphorus of 0.03 - 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.015 - 0.035 % |
EN 10269 Grade 35B2 quenched and tempered (+QT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2.17E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.62E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.32E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.2E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.23E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.41E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 7.8E-7 Ω·m |
EN 10269 Grade 35B2 quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 205 - 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 195 - 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 - 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 22 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Medium Carbon Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 45 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 500 - 650 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 280 - 300 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 300 MPa |
- |
| - |
50.0 °C |
Yield strength Rp0.2 of 287 - 289 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 255 - 270 MPa |
- |
| - |
150.0 °C |
Yield strength Rp0.2 of 235 - 251 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 220 - 229 MPa |
- |
| - |
250.0 °C |
Yield strength Rp0.2 of 203 - 213 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 186 - 192 MPa |
- |
| - |
350.0 °C |
Yield strength Rp0.2 of 167 - 182 MPa |
- |
| - |
400.0 °C |
Yield strength Rp0.2 of 147 - 173 MPa |
- |