EN 10269 Grade 25CrMo4 quenched and tempered (+QT)
EN 10269 Grade 25CrMo4 quenched and tempered (+QT) introduction
Steel 25CrMo4 is suitable for components with high strength and toughness requirements at mean and higher heat-treatment cross-sections in vehicle, engine and machine engineering (e.g. crankshafts, steering knuckles, pinions). Lowest working temperature -40 °C
Further application for mounting elements at increased and lower temperatures.
Equivalent material: NBN 25CrMo4, GB 30CrMoA, AFNOR 25CD4, BS 708M25, GOST 30ChM, ISO 25CrMo4, UNI 25CrMo4, JIS SCM430, PN C25HM, SS 2225, UNE F.1251-30CrMo4, ASTM 4130, DIN 25CrMo4, AISI 4130, SAE 4130, UNS G41300, GB 30CrMo, GB A30302, DIN KG, DIN 1.7214, AFNOR 25 CD 4 S, AFNOR 9160C083, AFNOR 9160/C 39, AFNOR 25CrMo4, BS FE-PL1502, BS 25CrMo4, EN 1.7214, UNS J24056, IS 26Cr4Mo2, DIN 1.7218, BS 1717CDS110, BS 708A25, UNI 25CrMo4(KB), UNE 55Cr3, AISI 4130H, SAE 4130H, JIS SM420, JIS SCM420, JIS SCCrM1A, JIS SCCrM1B, EN 1.7218, ASTM 4130H, UNS H41300
EN 10269 Grade 25CrMo4 quenched and tempered (+QT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.83 - 7.85 g/cm³ |
EN 10269 Grade 25CrMo4 quenched and tempered (+QT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.15E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.11E-5 - 1.21E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.21E-5 - 1.27E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.29E-5 - 1.32E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.35E-5 - 1.36E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.4E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.44E-5 1/K |
- |
| Max service temperature, long |
- |
Max service temperature, long of -40 - 200 °C |
- |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Molybdenum Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 41 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 11.1 - 42.7 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 12.1 - 42.8 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 12.9 - 41.6 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 39.9 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 37.8 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 35.6 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 11.4 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 11 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 10.3 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 9.5 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.5 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.3 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 6 mm²/s |
- |
EN 10269 Grade 25CrMo4 quenched and tempered (+QT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.22 - 0.29 % |
| Chromium |
Chromium of 0.9 - 1.2 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Molybdenum |
Molybdenum of 0.15 - 0.3 % |
| Phosphorus |
Phosphorus of 0.03 - 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10269 Grade 25CrMo4 quenched and tempered (+QT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2.54E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 3E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.69E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.51E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.45E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.54E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 7.78E-7 Ω·m |
EN 10269 Grade 25CrMo4 quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 205 - 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 195 - 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 - 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 18 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Molybdenum Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 60 % |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 600 - 750 MPa |
- |
| - |
300.0 °C |
Tensile strength of 460 MPa |
- |
| - |
350.0 °C |
Tensile strength of 440 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 420 - 440 MPa |
- |
| - |
50.0 °C |
Yield strength Rp0.2 of 414 - 435 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 403 - 428 MPa |
- |
| - |
150.0 °C |
Yield strength Rp0.2 of 393 - 420 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 382 - 412 MPa |
- |
| - |
250.0 °C |
Yield strength Rp0.2 of 372 - 392 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 344 - 363 MPa |
- |
| - |
350.0 °C |
Yield strength Rp0.2 of 324 - 333 MPa |
- |
| - |
400.0 °C |
Yield strength Rp0.2 of 294 - 304 MPa |
- |
| - |
450.0 °C |
Yield strength Rp0.2 of 265 - 275 MPa |
- |
| - |
500.0 °C |
Yield strength Rp0.2 of 226 - 235 MPa |
- |
Stay ahead of the curve with our advanced steel technologies that push boundaries and unlock new possibilities.
-- Our promise
Similar or equivalent steel materials