EN 10268 Grade HC380LA
EN 10268 Grade HC380LA introduction
This high strength steel is characterised by their low content of both carbon and micro-alloying elements. This gives HSLA steels outstanding functional properties, such as weldability and coatability. The hardening achieved by controlled internal purity and fine grain size structure ensures excellent mechanical strength. The grade available is in compliance with EN 10268:2006+A1:2013 and are obtained after either batch or continuous annealing. The grade with yield strength ≥ 460 MPa are only produced by the continuous annealing process.
EN 10268 Grade HC380LA chemical
| Property | Value | Comment |
|---|---|---|
| Aluminium | Aluminium of 0.015 % | min. |
| Carbon | Carbon of 0.12 % | max. |
| Manganese | Manganese of 1.6 % | max. |
| Niobium | Niobium of 0.09 % | max. |
| Phosphorus | Phosphorus of 0.03 % | max. |
| Silicon | Silicon of 0.5 % | max. |
| Sulfur | Sulfur of 0.025 % | max. |
| Titanium | Titanium of 0.15 % | max. |
EN 10268 Grade HC380LA mechanical
| Property | Value | Comment |
|---|---|---|
| Elongation | Elongation of 17 % | min. | for thickness 0.5-0.7 mm | A80 | Transverse |
| - | Elongation of 18 % | min. | for thickness 0.5-0.7 mm | A80 |
| - | Elongation of 19 % | min. | for thickness 0.7-3 mm | A80 | Transverse |
| - | Elongation of 20 % | min. | for thickness 0.7-3 mm | A80 |
| Tensile strength | Tensile strength of 430 - 550 MPa | for thickness 0.5-3 mm |
| - | Tensile strength of 440 - 580 MPa | for thickness 0.5-3 mm | Transverse |
| Yield strength | Yield strength of 350 - 450 MPa | for thickness 0.5-3 mm |
| - | Yield strength of 380 - 480 MPa | for thickness 0.5-3 mm | Transverse |