EN 10217-7 Grade X1NiCrMoCu31-27-4 solution annealed (+AT)
EN 10217-7 Grade X1NiCrMoCu31-27-4 solution annealed (+AT) introduction
The austenitic steel X1NiCrMoCu31-27-4 is available in the solution annealed condition. Welded circular tubes of this steel are used for compression load and for corrosive load at room temperature, low temperatures and elevated temperatures. The material is resistant to intercrystalline corrosion (up to 400 °C) also in the welded condition.
Equivalent material: UNS N08028, DIN X1NiCrMoCuN31-27-4, DIN 1.4563, AFNOR Z2NCDU31-27, EN 1.4563
EN 10217-7 Grade X1NiCrMoCu31-27-4 solution annealed (+AT) general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 8 - 8.08 g/cm³ |
EN 10217-7 Grade X1NiCrMoCu31-27-4 solution annealed (+AT) thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 100.0 °C | Coefficient of thermal expansion of 1.51E-5 - 1.58E-5 1/K | - |
| - | 200.0 °C | Coefficient of thermal expansion of 1.55E-5 - 1.61E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.58E-5 - 1.65E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.62E-5 - 1.69E-5 1/K | - |
| - | 500.0 °C | Coefficient of thermal expansion of 1.66E-5 - 1.73E-5 1/K | - |
| Melting point | - | Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel |
| Specific heat capacity | 20.0 °C | Specific heat capacity of 450 - 452 J/(kg·K) | - |
| - | 100.0 °C | Specific heat capacity of 463 J/(kg·K) | - |
| - | 200.0 °C | Specific heat capacity of 474 J/(kg·K) | - |
| - | 300.0 °C | Specific heat capacity of 483 J/(kg·K) | - |
| - | 400.0 °C | Specific heat capacity of 491 J/(kg·K) | - |
| - | 500.0 °C | Specific heat capacity of 500 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 11.7 - 12 W/(m·K) | - |
| - | 100.0 °C | Thermal conductivity of 13.2 W/(m·K) | - |
| - | 200.0 °C | Thermal conductivity of 15 W/(m·K) | - |
| - | 300.0 °C | Thermal conductivity of 16.8 W/(m·K) | - |
| - | 400.0 °C | Thermal conductivity of 18.5 W/(m·K) | - |
| - | 500.0 °C | Thermal conductivity of 20.2 W/(m·K) | - |
| Thermal diffusivity | 20.0 °C | Thermal diffusivity of 3.2 mm²/s | - |
| - | 100.0 °C | Thermal diffusivity of 3.5 mm²/s | - |
| - | 200.0 °C | Thermal diffusivity of 3.8 mm²/s | - |
| - | 300.0 °C | Thermal diffusivity of 4.1 mm²/s | - |
| - | 400.0 °C | Thermal diffusivity of 4.5 mm²/s | - |
| - | 500.0 °C | Thermal diffusivity of 4.8 mm²/s | - |
EN 10217-7 Grade X1NiCrMoCu31-27-4 solution annealed (+AT) chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.02 % |
| Chromium | Chromium of 26 - 28 % |
| Copper | Copper of 0.7 - 1.5 % |
| Manganese | Manganese of 2 % |
| Molybdenum | Molybdenum of 3 - 4 % |
| Nickel | Nickel of 30 - 32 % |
| Nitrogen | Nitrogen of 0.11 % |
| Phosphorus | Phosphorus of 0.03 % |
| Silicon | Silicon of 0.7 % |
| Sulfur | Sulfur of 0.01 % |
EN 10217-7 Grade X1NiCrMoCu31-27-4 solution annealed (+AT) electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 1E-6 - 1.04E-6 Ω·m |
| - | 100.0 °C | Electrical resistivity of 1.07E-6 Ω·m |
| - | 200.0 °C | Electrical resistivity of 1.1E-6 Ω·m |
| - | 300.0 °C | Electrical resistivity of 1.13E-6 Ω·m |
| - | 400.0 °C | Electrical resistivity of 1.16E-6 Ω·m |
| - | 500.0 °C | Electrical resistivity of 1.18E-6 Ω·m |
EN 10217-7 Grade X1NiCrMoCu31-27-4 solution annealed (+AT) mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 20.0 °C | Elastic modulus of 191 - 195 GPa | - |
| - | 100.0 °C | Elastic modulus of 186 - 190 GPa | - |
| - | 200.0 °C | Elastic modulus of 179 - 182 GPa | - |
| - | 300.0 °C | Elastic modulus of 172 - 174 GPa | - |
| - | 400.0 °C | Elastic modulus of 166 GPa | - |
| - | 500.0 °C | Elastic modulus of 158 - 159 GPa | - |
| Elongation | 20.0 °C | Elongation of 40 % | - |
| Elongation, transverse | 20.0 °C | Elongation, transverse of 35 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Austenitic Stainless Steel |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Austenitic Stainless Steel |
| Tensile strength | 20.0 °C | Tensile strength of 500 - 750 MPa | - |
| Tensile strength, transverse | 20.0 °C | Tensile strength, transverse of 500 - 750 MPa | - |
| Yield strength Rp0.2 | 20.0 °C | Yield strength Rp0.2 of 215 MPa | - |
| - | 50.0 °C | Yield strength Rp0.2 of 210 MPa | - |
| - | 100.0 °C | Yield strength Rp0.2 of 190 MPa | - |
| - | 150.0 °C | Yield strength Rp0.2 of 175 MPa | - |
| - | 200.0 °C | Yield strength Rp0.2 of 160 MPa | - |
| - | 250.0 °C | Yield strength Rp0.2 of 155 MPa | - |
| - | 300.0 °C | Yield strength Rp0.2 of 150 MPa | - |
| - | 350.0 °C | Yield strength Rp0.2 of 145 MPa | - |
| - | 400.0 °C | Yield strength Rp0.2 of 135 MPa | - |
| - | 450.0 °C | Yield strength Rp0.2 of 125 MPa | - |
| - | 500.0 °C | Yield strength Rp0.2 of 120 MPa | - |
| - | 550.0 °C | Yield strength Rp0.2 of 115 MPa | - |
| Yield strength Rp0.2, transverse | 20.0 °C | Yield strength Rp0.2, transverse of 215 MPa | - |
| Yield strength Rp1.0 | 20.0 °C | Yield strength Rp1.0 of 245 MPa | - |
| - | 50.0 °C | Yield strength Rp1.0 of 240 MPa | - |
| - | 100.0 °C | Yield strength Rp1.0 of 220 MPa | - |
| - | 150.0 °C | Yield strength Rp1.0 of 205 MPa | - |
| - | 200.0 °C | Yield strength Rp1.0 of 190 MPa | - |
| - | 250.0 °C | Yield strength Rp1.0 of 185 MPa | - |
| - | 300.0 °C | Yield strength Rp1.0 of 180 MPa | - |
| - | 350.0 °C | Yield strength Rp1.0 of 175 MPa | - |
| - | 400.0 °C | Yield strength Rp1.0 of 165 MPa | - |
| - | 450.0 °C | Yield strength Rp1.0 of 155 MPa | - |
| - | 500.0 °C | Yield strength Rp1.0 of 150 MPa | - |
| - | 550.0 °C | Yield strength Rp1.0 of 146 MPa | - |
Empower your construction projects with our dependable steel solutions.
-- Our promise
Similar or equivalent steel materials
- EN 10088-1 Grade X1NiCrMoCu31-27-4 solution annealed (+AT)
- EN 10272 Grade X1NiCrMoCu31-27-4 solution annealed (+AT)
- EN 10028-7 Grade X1NiCrMoCu31-27-4 solution annealed (+AT)
- EN 10216-5 Grade X1NiCrMoCu31-27-4 solution annealed (+AT)
- SEW 400 Grade X1NiCrMoCuN31-27-4 quenched (+Q)
- EN 10250-4 Grade X1NiCrMoCu31-27-4 solution annealed (+AT)