EN 10217-4 Grade P265NL normalized or normalized formed (+N)
EN 10217-4 Grade P265NL normalized or normalized formed (+N) introduction
Electrical welded tubes made of the non-alloy quality steel P265NL, which is low temperature resistant, are used first of all in the apparatus construction, reservoir construction, pipeline construction as well as in the general mechanical engineering and device construction.
The weldability is given.
Equivalent material: DIN 1.0453, EN 1.0453
EN 10217-4 Grade P265NL normalized or normalized formed (+N) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10217-4 Grade P265NL normalized or normalized formed (+N) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
EN 10217-4 Grade P265NL normalized or normalized formed (+N) chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Carbon |
Carbon of 0.2 % |
| Chromium |
Chromium of 0.3 % |
| Copper |
Copper of 0.3 % |
| Manganese |
Manganese of 0.6 - 1.4 % |
| Molybdenum |
Molybdenum of 0.08 % |
| Nickel |
Nickel of 0.3 % |
| Niobium |
Niobium of 0.01 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.02 % |
| Titanium |
Titanium of 0.04 % |
| Vanadium |
Vanadium of 0.02 % |
EN 10217-4 Grade P265NL normalized or normalized formed (+N) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10217-4 Grade P265NL normalized or normalized formed (+N) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10217-4 Grade P265NL normalized or normalized formed (+N) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation |
20.0 °C |
Elongation of 24 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 22 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 410 - 570 MPa |
- |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 410 - 570 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 265 MPa |
- |