EN 10217-2 Grade St37.8 normalized or normalized formed (+N)
EN 10217-2 Grade St37.8 normalized or normalized formed (+N) introduction
High temperature tube steel for welded tubes and tube products. Applicable up to 500 °C wall temperature for continuous operation.
Application:
vessel construction, apparatus construction, petrochemical industry
Equivalent material: ISO TW5, UNI Fe37, DIN 1.0315, EN 1.0315, ASTM C55
EN 10217-2 Grade St37.8 normalized or normalized formed (+N) general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.85 g/cm³ |
EN 10217-2 Grade St37.8 normalized or normalized formed (+N) thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | -100.0 °C | Coefficient of thermal expansion of 1.08E-5 1/K | - |
| - | 20.0 °C | Coefficient of thermal expansion of 1.19E-5 1/K | - |
| - | 100.0 °C | Coefficient of thermal expansion of 1.22E-5 - 1.25E-5 1/K | - |
| - | 200.0 °C | Coefficient of thermal expansion of 1.29E-5 - 1.3E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.34E-5 - 1.36E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.4E-5 - 1.41E-5 1/K | - |
| - | 500.0 °C | Coefficient of thermal expansion of 1.43E-5 - 1.45E-5 1/K | - |
| - | 600.0 °C | Coefficient of thermal expansion of 1.46E-5 - 1.49E-5 1/K | - |
| Max service temperature | - | Max service temperature of 500 °C | Typical for Carbon Steel |
| Max service temperature, long | - | Max service temperature, long of 0 - 500 °C | - |
| Melting point | - | Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
| Specific heat capacity | -100.0 °C | Specific heat capacity of 423 J/(kg·K) | - |
| - | 20.0 °C | Specific heat capacity of 461 J/(kg·K) | - |
| - | 100.0 °C | Specific heat capacity of 479 - 500 J/(kg·K) | - |
| - | 200.0 °C | Specific heat capacity of 499 - 540 J/(kg·K) | - |
| - | 300.0 °C | Specific heat capacity of 517 - 580 J/(kg·K) | - |
| - | 400.0 °C | Specific heat capacity of 536 - 620 J/(kg·K) | - |
| - | 500.0 °C | Specific heat capacity of 558 - 690 J/(kg·K) | - |
| - | 600.0 °C | Specific heat capacity of 587 - 780 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 56.9 W/(m·K) | - |
| - | 100.0 °C | Thermal conductivity of 56.4 - 57 W/(m·K) | - |
| - | 200.0 °C | Thermal conductivity of 53.5 - 54 W/(m·K) | - |
| - | 300.0 °C | Thermal conductivity of 49.4 - 50 W/(m·K) | - |
| - | 400.0 °C | Thermal conductivity of 45 - 45.2 W/(m·K) | - |
| - | 500.0 °C | Thermal conductivity of 41.3 - 42 W/(m·K) | - |
| - | 600.0 °C | Thermal conductivity of 37 - 37.6 W/(m·K) | - |
| Thermal diffusivity | 20.0 °C | Thermal diffusivity of 15.7 mm²/s | - |
| - | 100.0 °C | Thermal diffusivity of 14.5 mm²/s | - |
| - | 200.0 °C | Thermal diffusivity of 12.9 mm²/s | - |
| - | 300.0 °C | Thermal diffusivity of 11.2 mm²/s | - |
| - | 400.0 °C | Thermal diffusivity of 9.6 mm²/s | - |
| - | 500.0 °C | Thermal diffusivity of 7.9 mm²/s | - |
| - | 600.0 °C | Thermal diffusivity of 6.3 mm²/s | - |
EN 10217-2 Grade St37.8 normalized or normalized formed (+N) chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.17 % |
| Manganese | Manganese of 0.4 - 0.8 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 0.1 - 0.35 % |
| Sulfur | Sulfur of 0.04 % |
EN 10217-2 Grade St37.8 normalized or normalized formed (+N) magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
EN 10217-2 Grade St37.8 normalized or normalized formed (+N) electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 1.83E-7 Ω·m |
| - | 100.0 °C | Electrical resistivity of 2.27E-7 - 2.3E-7 Ω·m |
| - | 200.0 °C | Electrical resistivity of 2.95E-7 - 3E-7 Ω·m |
| - | 300.0 °C | Electrical resistivity of 3.8E-7 Ω·m |
| - | 400.0 °C | Electrical resistivity of 4.8E-7 - 4.81E-7 Ω·m |
| - | 500.0 °C | Electrical resistivity of 5.99E-7 - 6E-7 Ω·m |
| - | 600.0 °C | Electrical resistivity of 7.38E-7 - 7.4E-7 Ω·m |
EN 10217-2 Grade St37.8 normalized or normalized formed (+N) mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | -100.0 °C | Elastic modulus of 217 GPa | - |
| - | 20.0 °C | Elastic modulus of 212 GPa | - |
| - | 100.0 °C | Elastic modulus of 207 GPa | - |
| - | 200.0 °C | Elastic modulus of 199 - 200 GPa | - |
| - | 300.0 °C | Elastic modulus of 192 GPa | - |
| - | 400.0 °C | Elastic modulus of 183 - 184 GPa | - |
| - | 500.0 °C | Elastic modulus of 175 GPa | - |
| - | 600.0 °C | Elastic modulus of 164 - 166 GPa | - |
| Elongation | 20.0 °C | Elongation of 25 % | - |
| Elongation, transverse | 20.0 °C | Elongation, transverse of 23 % | - |
| Poisson's ratio | 20.0 °C | Poisson's ratio of 0.28 [-] | - |
| Shear modulus | 23.0 °C | Shear modulus of 82 GPa | Typical for Low Carbon Steel |
| Tensile strength | 20.0 °C | Tensile strength of 360 - 480 MPa | - |
| Yield strength Rp0.2 | 20.0 °C | Yield strength Rp0.2 of 235 MPa | - |
| - | 200.0 °C | Yield strength Rp0.2 of 185 MPa | - |
| - | 250.0 °C | Yield strength Rp0.2 of 165 MPa | - |
| - | 300.0 °C | Yield strength Rp0.2 of 140 MPa | - |
| - | 350.0 °C | Yield strength Rp0.2 of 120 MPa | - |
| - | 400.0 °C | Yield strength Rp0.2 of 110 MPa | - |
| - | 450.0 °C | Yield strength Rp0.2 of 105 MPa | - |