EN 10216-4 Grade P215NL normalized or normalized formed (+N)
EN 10216-4 Grade P215NL normalized or normalized formed (+N) introduction
Tubes made from cryogenic unalloyed quality steel P215NL are predominantly used in apparatus, tank, line construction as well as in general machine and equipment engineering.
Weldability is available.
Equivalent material: DIN P215NL, DIN TTSt35N, DIN 1.0451, EN 1.0451
EN 10216-4 Grade P215NL normalized or normalized formed (+N) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10216-4 Grade P215NL normalized or normalized formed (+N) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
EN 10216-4 Grade P215NL normalized or normalized formed (+N) chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Carbon |
Carbon of 0.15 % |
| Chromium |
Chromium of 0.3 % |
| Copper |
Copper of 0.3 % |
| Manganese |
Manganese of 0.4 - 1.2 % |
| Molybdenum |
Molybdenum of 0.08 % |
| Nickel |
Nickel of 0.3 % |
| Niobium |
Niobium of 0.01 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.35 % |
| Sulfur |
Sulfur of 0.01 - 0.02 % |
| Titanium |
Titanium of 0.04 % |
| Vanadium |
Vanadium of 0.02 % |
EN 10216-4 Grade P215NL normalized or normalized formed (+N) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10216-4 Grade P215NL normalized or normalized formed (+N) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10216-4 Grade P215NL normalized or normalized formed (+N) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation |
20.0 °C |
Elongation of 25 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 23 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 360 - 480 MPa |
- |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 360 - 480 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 215 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 175 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 145 MPa |
- |
| - |
250.0 °C |
Yield strength Rp0.2 of 130 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 115 MPa |
- |
| Yield strength Rp0.2, transverse |
20.0 °C |
Yield strength Rp0.2, transverse of 215 MPa |
- |
Experience the power of our premium steel, forged to perfection for exceptional performance.