EN 10213 Grade G9Ni14 quenched and tempered (+QT)
EN 10213 Grade G9Ni14 quenched and tempered (+QT) introduction
Material G9Ni14 is equivalent to trademark GS-10 Ni 14 acc. to SEW 685-89. It is applicated at low temperatures. It is used for refrigerating plants and fittings up to approx. -90 °C.
Equivalent material: STAS T15Ni35R, UNE AM8Ni14, UNE F.8374, MSZ Aö10Ni14, DIN GS-10Ni14, ISO G9Ni14, JIS SCPL31, KS SCPL31, ASTM LC3, UNS J31550, ASTM B3N, ASTM B3Q, UNS J31500, DIN G9Ni14, ASTM A352 Grade LC3, ASTM Grade LC3, ASTM A757 Grade B3N, ASTM A757 Grade B3Q, ASTM Grade B3N, ASTM Grade B3Q, DIN 1.5638, EN 1.5638
EN 10213 Grade G9Ni14 quenched and tempered (+QT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
EN 10213 Grade G9Ni14 quenched and tempered (+QT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-195.0 °C |
Coefficient of thermal expansion of 8.5E-6 1/K |
- |
| - |
-170.0 °C |
Coefficient of thermal expansion of 9E-6 1/K |
- |
| - |
-120.0 °C |
Coefficient of thermal expansion of 9.8E-6 1/K |
- |
| - |
-50.0 °C |
Coefficient of thermal expansion of 1.04E-5 1/K |
- |
| - |
-25.0 °C |
Coefficient of thermal expansion of 1.06E-5 1/K |
- |
| Max service temperature, long |
- |
Max service temperature, long of -90 - 0 °C |
- |
| Melting point |
- |
Melting point of 1316 - 1595 °C |
Typical for Nickel Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
- |
| Thermal conductivity |
-20.0 °C |
Thermal conductivity of 35 W/(m·K) |
- |
EN 10213 Grade G9Ni14 quenched and tempered (+QT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.06 - 0.12 % |
| Chromium |
Chromium of 0.3 % |
| Copper |
Copper of 0.3 % |
| Manganese |
Manganese of 0.5 - 0.8 % |
| Molybdenum |
Molybdenum of 0.2 % |
| Nickel |
Nickel of 3 - 4 % |
| Phosphorus |
Phosphorus of 0.02 % |
| Silicon |
Silicon of 0.6 % |
| Sulfur |
Sulfur of 0.015 % |
| Vanadium |
Vanadium of 0.05 % |
EN 10213 Grade G9Ni14 quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Nickel Steel |
| Elongation |
20.0 °C |
Elongation of 20 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Nickel Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 76 GPa |
Typical for Nickel Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 500 - 650 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 360 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 255 MPa |
- |
| - |
150.0 °C |
Yield strength Rp0.2 of 235 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 215 MPa |
- |
| - |
250.0 °C |
Yield strength Rp0.2 of 190 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 175 MPa |
- |