EN 10213-4 Grade GX5CrNiMoNb19-11-2 solution heat-treated and quenched
EN 10213-4 Grade GX5CrNiMoNb19-11-2 solution heat-treated and quenched introduction
The austenitic material GX5CrNiMoNb19-11-2 is equivalent to trademark G-X 5CrNiMoNb 18 10 acc. to DIN 17445-84. This ic-resistant material is used for fittings, pumps, agitators, tanks in chemical industry, in cellulose, rayon staple, textile, color and rubber industry. It is weldable without preheating and heat after treatment. A special stabilization annealing in a range from 550 to 600 °C. is accordable in order to improve the corrosion resistance.
Equivalent material: BS 318C17, UNI GX6CrNiMoNb20-11, JIS SCS22, JUS CL4574, STAS T10MoNiCr180, MSZ AöX10CrNiMoNb18-12, DIN G-X5CrNiMoNb18-10, DIN 1.4581, DIN GX5CrNiMoNb19-11-2, AISI 316Ti, SAE 316Ti, JIS TW61, EN 1.4581
EN 10213-4 Grade GX5CrNiMoNb19-11-2 solution heat-treated and quenched general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.9 g/cm³ |
EN 10213-4 Grade GX5CrNiMoNb19-11-2 solution heat-treated and quenched thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.58E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.77E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 530 J/(kg·K) |
- |
| Thermal conductivity |
50.0 °C |
Thermal conductivity of 14.5 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 15.8 W/(m·K) |
- |
EN 10213-4 Grade GX5CrNiMoNb19-11-2 solution heat-treated and quenched chemical
| Property |
Value |
| Carbon |
Carbon of 0.07 % |
| Chromium |
Chromium of 18 - 20 % |
| Manganese |
Manganese of 1.5 % |
| Molybdenum |
Molybdenum of 2 - 2.5 % |
| Nickel |
Nickel of 9 - 12 % |
| Niobium |
Niobium of 1 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1.5 % |
| Sulfur |
Sulfur of 0.03 % |
EN 10213-4 Grade GX5CrNiMoNb19-11-2 solution heat-treated and quenched electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
EN 10213-4 Grade GX5CrNiMoNb19-11-2 solution heat-treated and quenched mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation |
20.0 °C |
Elongation of 25 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 440 - 640 MPa |
- |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 210 MPa |
- |
| - |
100.0 °C |
Yield strength Rp1.0 of 185 MPa |
- |
| - |
200.0 °C |
Yield strength Rp1.0 of 160 MPa |
- |
| - |
300.0 °C |
Yield strength Rp1.0 of 145 MPa |
- |
| - |
400.0 °C |
Yield strength Rp1.0 of 130 MPa |
- |
| - |
500.0 °C |
Yield strength Rp1.0 of 120 MPa |
- |
| - |
550.0 °C |
Yield strength Rp1.0 of 115 MPa |
- |