EN 10213-4 Grade GX2CrNiMoN26-7-4 solution heat-treated and quenched
EN 10213-4 Grade GX2CrNiMoN26-7-4 solution heat-treated and quenched introduction
Material GX2CrNiMoN26-7-4 is equivalent to trademark G-X 2 CrNiMoN 25 7 4 acc. to SEW 410-88. This DIN-make is applicated for castings, e.g. in pump construction, for increased demands, especially for higher hydrosulfide-partial pressures and/or temperatures in sea and brackish water. G-X 2 CrNiMoN shows increased strength properties. It is unsuitable for operating temperatures above 300 deg.
Equivalent material: DIN G-X2CrNiMoN25-7-4, DIN 1.4469, EN 1.4469
EN 10213-4 Grade GX2CrNiMoN26-7-4 solution heat-treated and quenched general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.7 g/cm³ |
EN 10213-4 Grade GX2CrNiMoN26-7-4 solution heat-treated and quenched thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 100.0 °C | Coefficient of thermal expansion of 1.3E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.4E-5 1/K | - |
| Max service temperature | - | Max service temperature of 300 °C | Typical for Duplex Stainless Steel |
| Melting point | - | Melting point of 1375 - 1450 °C | Typical for Duplex Stainless Steel |
| Specific heat capacity | 20.0 °C | Specific heat capacity of 450 J/(kg·K) | - |
| Thermal conductivity | 50.0 °C | Thermal conductivity of 17 W/(m·K) | - |
| - | 100.0 °C | Thermal conductivity of 18 W/(m·K) | - |
EN 10213-4 Grade GX2CrNiMoN26-7-4 solution heat-treated and quenched chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.03 % |
| Chromium | Chromium of 25 - 27 % |
| Copper | Copper of 1.3 % |
| Manganese | Manganese of 1 % |
| Molybdenum | Molybdenum of 3 - 5 % |
| Nickel | Nickel of 6 - 8 % |
| Nitrogen | Nitrogen of 0.12 - 0.22 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.025 % |
EN 10213-4 Grade GX2CrNiMoN26-7-4 solution heat-treated and quenched mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 200 GPa | Typical for Duplex Stainless Steel |
| Elongation | 20.0 °C | Elongation of 22 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Duplex Stainless Steel |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Duplex Stainless Steel |
| Tensile strength | 20.0 °C | Tensile strength of 650 - 850 MPa | - |
| Yield strength Rp0.2 | 20.0 °C | Yield strength Rp0.2 of 480 MPa | - |
| - | 100.0 °C | Yield strength Rp0.2 of 390 MPa | - |