EN 10213-4 Grade GX2CrNiMoCuN25-6-3-3 solution heat-treated and quenched
EN 10213-4 Grade GX2CrNiMoCuN25-6-3-3 solution heat-treated and quenched introduction
Material GX2CrNiMoCuN25-6-3-3 is equivalent to trademark G-X 3 CrNiMoCuN 26 63 3 acc. to SEW 410-88. The SEW-material shows higher resistance especially in the presence of non-oxidizing acids (e.g. sulfuric acid). It has increased strength properties and is unsuitable for operating temperatures above 300 °C. G-X 3 CrNiMoCuN 26 6 3 3 is used for castings for flue gas desulfurization.
Equivalent material: DIN G-X3CrNiMoCuN26-6-3-3, UNS J93404, DIN 1.4517, EN 1.4517
EN 10213-4 Grade GX2CrNiMoCuN25-6-3-3 solution heat-treated and quenched general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.7 g/cm³ |
EN 10213-4 Grade GX2CrNiMoCuN25-6-3-3 solution heat-treated and quenched thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.4E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 300 °C |
Typical for Duplex Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Duplex Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
50.0 °C |
Thermal conductivity of 17 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 18 W/(m·K) |
- |
EN 10213-4 Grade GX2CrNiMoCuN25-6-3-3 solution heat-treated and quenched chemical
| Property |
Value |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 24.5 - 26.5 % |
| Copper |
Copper of 2.75 - 3.5 % |
| Manganese |
Manganese of 1.5 % |
| Molybdenum |
Molybdenum of 2.5 - 3.5 % |
| Nickel |
Nickel of 5 - 7 % |
| Nitrogen |
Nitrogen of 0.12 - 0.22 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.025 % |
EN 10213-4 Grade GX2CrNiMoCuN25-6-3-3 solution heat-treated and quenched mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
Typical for Duplex Stainless Steel |
| Elongation |
20.0 °C |
Elongation of 22 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Duplex Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Duplex Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 650 - 850 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 480 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 390 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 330 MPa |
- |
Let our high-quality steel materials be the foundation of your architectural masterpieces and engineering marvels.