EN 10209 Grade DC06EK cold rolled, skin passed
EN 10209 Grade DC06EK cold rolled, skin passed introduction
Cold rolled low carbon steel for flat products for vitreous enamelling (one or two coats of conventional enamelling).
Application: domestic appliances (cooking, laundry), sanitary ware (bathtubs, shower trays, sinks), architectural panels (interior and exterior), signage
Equivalent material: ASTM A424TypeIII, DIN 1.0869, EN 1.0869, DIN DC06EK, AFNOR DC06EK, BS DC06EK, GB/T RT1, GB/T DC05EK, GB/T U43072
EN 10209 Grade DC06EK cold rolled, skin passed general
| Property |
Value |
Comment |
| Density |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10209 Grade DC06EK cold rolled, skin passed thermal
| Property |
Value |
Comment |
| Coefficient of thermal expansion |
Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
Max service temperature of 406.7 °C |
Predicted Value, Long |
| - |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
EN 10209 Grade DC06EK cold rolled, skin passed chemical
| Property |
Value |
Condition |
Related Standards |
Shape |
| Carbon |
Carbon of 0.02 % |
cold rolled, skin passed |
EN 10209 |
Sheet |
| Manganese |
Manganese of 0.5 % |
cold rolled, skin passed |
EN 10209 |
Sheet |
| Phosphorus |
Phosphorus of 0.02 % |
cold rolled, skin passed |
EN 10209 |
Sheet |
| Sulfur |
Sulfur of 0.05 % |
cold rolled, skin passed |
EN 10209 |
Sheet |
| Titanium |
Titanium of 0.3 % |
cold rolled, skin passed |
EN 10209 |
Sheet |
EN 10209 Grade DC06EK cold rolled, skin passed magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10209 Grade DC06EK cold rolled, skin passed electrical
| Property |
Value |
Comment |
| Electrical conductivity |
Electrical conductivity of 8 S/m |
Predicted Value |
| Electrical resistivity |
Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m |
Typical for Carbon Steel |
EN 10209 Grade DC06EK cold rolled, skin passed mechanical
| Property |
Temperature |
Value |
Condition |
Related Standards |
Shape |
Comment |
| Elastic modulus |
- |
Elastic modulus of 200 - 215 GPa |
- |
- |
- |
Typical for Low Carbon Steel |
| Elongation |
- |
Elongation of 14.4 % |
- |
- |
- |
Predicted Value, A200 |
| - |
- |
Elongation of 19.9 % |
- |
- |
- |
Predicted Value, A5 |
| - |
- |
Elongation of 21.3 % |
- |
- |
- |
Predicted Value, A50 |
| - |
- |
Elongation of 21.4 % |
- |
- |
- |
Predicted Value, Transverse |
| - |
- |
Elongation of 21.6 % |
- |
- |
- |
Predicted Value |
| - |
20 °C |
Elongation of 34 % |
cold rolled, skin passed |
EN 10209 |
Sheet |
A80 Transverse |
| - |
20 °C |
Elongation of 36 % |
cold rolled, skin passed |
EN 10209 |
Sheet |
A80 Transverse |
| - |
20 °C |
Elongation of 38 % |
cold rolled, skin passed |
EN 10209 |
Sheet |
A80 Transverse |
| - |
20 °C |
Elongation of 38 % |
cold rolled, skin passed |
EN 10209 |
Strip, Bar |
A80 |
| Hardness, Brinell |
- |
Hardness, Brinell of 269 [-] |
- |
- |
- |
Predicted Value, Transverse |
| Poisson's ratio |
- |
Poisson's ratio of 0.29 [-] |
- |
- |
- |
Typical for Low Carbon Steel |
| Reduction of area |
- |
Reduction of area of 40.5 % |
- |
- |
- |
Predicted Value |
| - |
- |
Reduction of area of 43.4 % |
- |
- |
- |
Predicted Value, Transverse |
| Shear modulus |
- |
Shear modulus of 82 GPa |
- |
- |
- |
Typical for Low Carbon Steel |
| Shear strength |
- |
Shear strength of 563.2 MPa |
- |
- |
- |
Predicted Value |
| Tensile strength |
20 °C |
Tensile strength of 270 - 350 MPa |
cold rolled, skin passed |
EN 10209 |
Sheet |
Transverse |
| - |
20 °C |
Tensile strength of 270 - 350 MPa |
cold rolled, skin passed |
EN 10209 |
Strip, Bar |
- |
| Yield strength |
- |
Yield strength of 286.4 MPa |
- |
- |
- |
Predicted Value, RP1 Transverse |
| - |
- |
Yield strength of 293.4 MPa |
- |
- |
- |
Predicted Value, RP1 |
| - |
- |
Yield strength of 331.1 MPa |
- |
- |
- |
Predicted Value, RP05 |
| - |
- |
Yield strength of 375.9 MPa |
- |
- |
- |
Predicted Value, RP02 Transverse |
| - |
- |
Yield strength of 548.4 MPa |
- |
- |
- |
Predicted Value, RP02 |
| - |
- |
Yield strength of 628.3 MPa |
- |
- |
- |
Predicted Value, RP002 |
| - |
20 °C |
Yield strength of 120 - 230 MPa |
cold rolled, skin passed |
EN 10209 |
Sheet |
Transverse |
| - |
20 °C |
Yield strength of 120 - 210 MPa |
cold rolled, skin passed |
EN 10209 |
Sheet |
Transverse |
| - |
20 °C |
Yield strength of 120 - 190 MPa |
cold rolled, skin passed |
EN 10209 |
Sheet |
Transverse |
| - |
20 °C |
Yield strength of 120 - 190 MPa |
cold rolled, skin passed |
EN 10209 |
Strip, Bar |
- |