EN 10208-2 Grade L450MB thermomechanically rolled
EN 10208-2 Grade L450MB thermomechanically rolled introduction
Steel L450MB is produced as welded pipe for flammable media in condition thermomechanically rolled formed. Its yield stress is between 450 and 570 N/mm². The steel is weldable, its carbon equivalent CEV accounts for max. 0.43. To the welding seam (welding methods SAW, COW) applies a mandrel-diameter for the bending test of 6x nominal thickness of the pipe.
Pipes are available with interior and exterior coating.
Main fields of application are long-distance pipelines for flammable liquids (e.g. crude oil and natural gas products) as well as for compressed and liquefied flammable gases. Pipes acc. to DIN EN 10208-2 : 1996-08 also fulfil the conditions decisive for the consumption acc. to standards 5L, 5LX and 5LS of the American Petroleum Institute (API). When using these pipes has to be considered the Technical rule for flammable liquids (Technische Regel für brennbare FlüssigkeitenTRbF 301).
Equivalent material: AFNOR TSE450, ISO L45TMC, DIN StE445.7TM, ISO X65ME, ISO L450ME, DIN 1.8975, DIN StE 445.7 TM, EN 1.8975
EN 10208-2 Grade L450MB thermomechanically rolled general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Steel |
EN 10208-2 Grade L450MB thermomechanically rolled chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.015 - 0.06 % |
| Carbon |
Carbon of 0.16 % |
| Chromium |
Chromium of 0.3 % |
| Copper |
Copper of 0.25 % |
| Manganese |
Manganese of 1.6 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.3 % |
| Niobium |
Niobium of 0.05 % |
| Nitrogen |
Nitrogen of 0.01 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.45 % |
| Sulfur |
Sulfur of 0.02 % |
| Titanium |
Titanium of 0.06 % |
| Vanadium |
Vanadium of 0.1 % |
EN 10208-2 Grade L450MB thermomechanically rolled mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
Typical for Steel |
| Elongation |
20.0 °C |
Elongation of 20 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 18 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 535 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 450 - 570 MPa |
- |
| Yield strength Rp0.5 |
20.0 °C |
Yield strength Rp0.5 of 450 - 570 MPa |
- |