EN 10207 Grade P275SL normalized or normalized formed (+N)
EN 10207 Grade P275SL normalized or normalized formed (+N) introduction
The non-alloy special steel P275SL is used for simple pressure vessels in the form of normalised or normalising rolled plates, strips and bars.
According the directive 87/404/EEC simple pressure vessels are defined as:
- every welded, cylindrical vessel with convex and/or flat bottoms made of unalloyed steel with internal pressures between min. 0.5 bar and max. 30 bar, used for air and nitrogen, not exposed to flames
- the product of pressure and capacity amounts to max. 10000 bar*l
Equivalent material: DIN P275SL, DIN 1.1100, EN 1.1100, JIS SPH275
EN 10207 Grade P275SL normalized or normalized formed (+N) general
| Property | Value | Comment |
|---|---|---|
| Density | Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
EN 10207 Grade P275SL normalized or normalized formed (+N) thermal
| Property | Value | Comment |
|---|---|---|
| Coefficient of thermal expansion | Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K | Typical for Low Carbon Steel |
| Max service temperature | Max service temperature of 303.3 °C | Predicted Value, Long |
| - | Max service temperature of 500 °C | Typical for Carbon Steel |
| Melting point | Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
| Specific heat capacity | Specific heat capacity of 465 J/(kg·K) | Typical for Low Carbon Steel |
| Thermal conductivity | Thermal conductivity of 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
EN 10207 Grade P275SL normalized or normalized formed (+N) chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Aluminium | Aluminium of 0.02 % | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar |
| Carbon | Carbon of 0.16 % | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar |
| Manganese | Manganese of 0.5 - 1.5 % | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar |
| Phosphorus | Phosphorus of 0.025 % | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar |
| Silicon | Silicon of 0.4 % | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar |
| Sulfur | Sulfur of 0.02 % | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar |
EN 10207 Grade P275SL normalized or normalized formed (+N) magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
EN 10207 Grade P275SL normalized or normalized formed (+N) electrical
| Property | Value | Comment |
|---|---|---|
| Electrical conductivity | Electrical conductivity of 7 S/m | Predicted Value |
| Electrical resistivity | Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m | Typical for Carbon Steel |
EN 10207 Grade P275SL normalized or normalized formed (+N) mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | - | Elastic modulus of 200 - 215 GPa | - | - | - | Typical for Low Carbon Steel |
| Elongation | - | Elongation of 18.2 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 19.7 % | - | - | - | Predicted Value, A5 |
| - | - | Elongation of 20.4 % | - | - | - | Predicted Value, A80 Transverse |
| - | - | Elongation of 23.7 % | - | - | - | Predicted Value, Transverse |
| - | - | Elongation of 24.8 % | - | - | - | Predicted Value, A50 |
| - | 20 °C | Elongation of 19 % | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | A80 |
| - | 20 °C | Elongation of 20 % | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | A80 |
| - | 20 °C | Elongation of 24 % | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | - |
| Hardness, Brinell | - | Hardness, Brinell of 239 [-] | - | - | - | Predicted Value, Transverse |
| Poisson's ratio | - | Poisson's ratio of 0.29 [-] | - | - | - | Typical for Low Carbon Steel |
| Reduction of area | - | Reduction of area of 42.4 % | - | - | - | Predicted Value, Transverse |
| - | - | Reduction of area of 43.2 % | - | - | - | Predicted Value |
| Shear modulus | - | Shear modulus of 82 GPa | - | - | - | Typical for Low Carbon Steel |
| Shear strength | - | Shear strength of 519.3 MPa | - | - | - | Predicted Value |
| Tensile strength | 20 °C | Tensile strength of 390 - 510 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | - |
| Yield strength | - | Yield strength of 259.3 MPa | - | - | - | Predicted Value, RP1 |
| - | - | Yield strength of 314.8 MPa | - | - | - | Predicted Value, Transverse |
| - | - | Yield strength of 316.9 MPa | - | - | - | Predicted Value, RP05 |
| - | - | Yield strength of 337.4 MPa | - | - | - | Predicted Value, RP1 Transverse |
| - | - | Yield strength of 451.8 MPa | - | - | - | Predicted Value, RP002 |
| - | - | Yield strength of 470.5 MPa | - | - | - | Predicted Value, RP02 Transverse |
| - | 20 °C | Yield strength of 255 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | - |
| - | 20 °C | Yield strength of 265 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | - |
| - | 20 °C | Yield strength of 275 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | - |
| - | 100 °C | Yield strength of 212 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | RP02 |
| - | 100 °C | Yield strength of 221 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | RP02 |
| - | 150 °C | Yield strength of 194 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | RP02 |
| - | 150 °C | Yield strength of 203 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | RP02 |
| - | 200 °C | Yield strength of 176 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | RP02 |
| - | 250 °C | Yield strength of 159 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | RP02 |
| - | 300 °C | Yield strength of 132 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | RP02 |