EN 10207 Grade P265S normalized or normalized formed (+N)
EN 10207 Grade P265S normalized or normalized formed (+N) introduction
The non-alloy quality steel P265S is used for simple pressure vessels in the form of normalised or normalising rolled plates, strips and bars.
According the directive 87/404/EEC simple pressure vessels are defined as:
- every welded, cylindrical vessel with convex and/or flat bottoms made of unalloyed steel with internal pressures between min. 0.5 bar and max. 30 bar, used for air and nitrogen, not exposed to flames
- the product of pressure and capacity amounts to max. 10000 bar*l
Equivalent material: DIN P265S, DIN 1.0130, EN 1.0130, DIN SPH 265, AFNOR P265S, BS P265S, JIS SPH265
EN 10207 Grade P265S normalized or normalized formed (+N) general
| Property | Value | Comment |
|---|---|---|
| Density | Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
EN 10207 Grade P265S normalized or normalized formed (+N) thermal
| Property | Value | Comment |
|---|---|---|
| Coefficient of thermal expansion | Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K | Typical for Low Carbon Steel |
| Max service temperature | Max service temperature of 344.8 °C | Predicted Value, Long |
| - | Max service temperature of 500 °C | Typical for Carbon Steel |
| Melting point | Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
| Specific heat capacity | Specific heat capacity of 465 J/(kg·K) | Typical for Low Carbon Steel |
| Thermal conductivity | Thermal conductivity of 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
EN 10207 Grade P265S normalized or normalized formed (+N) chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Aluminium | Aluminium of 0.02 % | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar |
| Carbon | Carbon of 0.2 % | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar |
| Manganese | Manganese of 0.5 - 1.5 % | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar |
| Phosphorus | Phosphorus of 0.025 % | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar |
| Silicon | Silicon of 0.4 % | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar |
| Sulfur | Sulfur of 0.025 % | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar |
EN 10207 Grade P265S normalized or normalized formed (+N) magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
EN 10207 Grade P265S normalized or normalized formed (+N) electrical
| Property | Value | Comment |
|---|---|---|
| Electrical conductivity | Electrical conductivity of 7 S/m | Predicted Value |
| Electrical resistivity | Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m | Typical for Carbon Steel |
EN 10207 Grade P265S normalized or normalized formed (+N) mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | - | Elastic modulus of 200 - 215 GPa | - | - | - | Typical for Low Carbon Steel |
| Elongation | - | Elongation of 18.4 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 19.2 % | - | - | - | Predicted Value, A80 Transverse |
| - | - | Elongation of 20.7 % | - | - | - | Predicted Value, A5 |
| - | - | Elongation of 22.0 % | - | - | - | Predicted Value, Transverse |
| - | - | Elongation of 24.1 % | - | - | - | Predicted Value, A50 |
| - | 20 °C | Elongation of 17 % | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | A80 |
| - | 20 °C | Elongation of 18 % | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | A80 |
| - | 20 °C | Elongation of 22 % | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | - |
| Hardness, Brinell | - | Hardness, Brinell of 243 [-] | - | - | - | Predicted Value, Transverse |
| Poisson's ratio | - | Poisson's ratio of 0.29 [-] | - | - | - | Typical for Low Carbon Steel |
| Reduction of area | - | Reduction of area of 43.3 % | - | - | - | Predicted Value |
| - | - | Reduction of area of 43.7 % | - | - | - | Predicted Value, Transverse |
| Shear modulus | - | Shear modulus of 82 GPa | - | - | - | Typical for Low Carbon Steel |
| Shear strength | - | Shear strength of 527.8 MPa | - | - | - | Predicted Value |
| Tensile strength | 20 °C | Tensile strength of 410 - 530 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | - |
| Yield strength | - | Yield strength of 252.6 MPa | - | - | - | Predicted Value, RP1 |
| - | - | Yield strength of 304 MPa | - | - | - | Predicted Value, RP05 |
| - | - | Yield strength of 314.6 MPa | - | - | - | Predicted Value, Transverse |
| - | - | Yield strength of 315.9 MPa | - | - | - | Predicted Value, RP1 Transverse |
| - | - | Yield strength of 452.6 MPa | - | - | - | Predicted Value, RP002 |
| - | - | Yield strength of 471.1 MPa | - | - | - | Predicted Value, RP02 Transverse |
| - | 20 °C | Yield strength of 245 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | - |
| - | 20 °C | Yield strength of 255 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | - |
| - | 20 °C | Yield strength of 265 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | - |
| - | 100 °C | Yield strength of 194 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | RP02 |
| - | 150 °C | Yield strength of 185 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | RP02 |
| - | 200 °C | Yield strength of 176 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | RP02 |
| - | 250 °C | Yield strength of 158 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | RP02 |
| - | 300 °C | Yield strength of 140 MPa | normalized or normalized formed (+N) | EN 10207 | Strip, Sheet, Bar | RP02 |