EN 10149-3 Grade S315NC normalized or normalized formed (+N)
EN 10149-3 Grade S315NC normalized or normalized formed (+N) introduction
Normalized or normalized rolled, weldable steel for cold formed components like vehicle frames, axles and special sections.
Equivalent material: BS HR40/30, IS FeE315, ASTM HSLAS-F Grade 50, DIN QStE300N, DIN 1.0973, EN QStE 300 N, EN 1.0973, DIN QStE 300 N, DIN S315NC, AFNOR S315NC, BS 40/30HR, BS 40/30CS, BS 40/30HS, BS S315NC
EN 10149-3 Grade S315NC normalized or normalized formed (+N) general
| Property |
Value |
Comment |
| Density |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10149-3 Grade S315NC normalized or normalized formed (+N) thermal
| Property |
Value |
Condition |
Related Standards |
Shape |
Comment |
| Coefficient of thermal expansion |
Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K |
- |
- |
- |
Typical for Low Carbon Steel |
| Max service temperature |
Max service temperature of -20 °C |
normalized or normalized formed (+N) |
EN 10149-3 |
Flat |
Long |
| - |
Max service temperature of 500 °C |
- |
- |
- |
Typical for Carbon Steel |
| Melting point |
Melting point of 1480 - 1526 °C |
- |
- |
- |
Typical for Low Carbon Steel |
| Specific heat capacity |
Specific heat capacity of 465 J/(kg·K) |
- |
- |
- |
Typical for Low Carbon Steel |
| Thermal conductivity |
Thermal conductivity of 25 - 93 W/(m·K) |
- |
- |
- |
Typical for Low Carbon Steel |
EN 10149-3 Grade S315NC normalized or normalized formed (+N) chemical
| Property |
Value |
Condition |
Related Standards |
Shape |
| Aluminium |
Aluminium of 0.015 % |
normalized or normalized formed (+N) |
EN 10149-3 |
Flat |
| Carbon |
Carbon of 0.16 % |
normalized or normalized formed (+N) |
EN 10149-3 |
Flat |
| Manganese |
Manganese of 1.4 % |
normalized or normalized formed (+N) |
EN 10149-3 |
Flat |
| Niobium |
Niobium of 0.09 % |
normalized or normalized formed (+N) |
EN 10149-3 |
Flat |
| Phosphorus |
Phosphorus of 0.025 % |
normalized or normalized formed (+N) |
EN 10149-3 |
Flat |
| Silicon |
Silicon of 0.5 % |
normalized or normalized formed (+N) |
EN 10149-3 |
Flat |
| Sulfur |
Sulfur of 0.02 % |
normalized or normalized formed (+N) |
EN 10149-3 |
Flat |
| Titanium |
Titanium of 0.15 % |
normalized or normalized formed (+N) |
EN 10149-3 |
Flat |
| Vanadium |
Vanadium of 0.1 % |
normalized or normalized formed (+N) |
EN 10149-3 |
Flat |
EN 10149-3 Grade S315NC normalized or normalized formed (+N) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10149-3 Grade S315NC normalized or normalized formed (+N) electrical
| Property |
Value |
Comment |
| Electrical conductivity |
Electrical conductivity of 7 S/m |
Predicted Value |
| Electrical resistivity |
Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m |
Typical for Carbon Steel |
EN 10149-3 Grade S315NC normalized or normalized formed (+N) mechanical
| Property |
Temperature |
Value |
Condition |
Related Standards |
Shape |
Comment |
| Elastic modulus |
- |
Elastic modulus of 200 - 215 GPa |
- |
- |
- |
Typical for Low Carbon Steel |
| Elongation |
- |
Elongation of 18.1 % |
- |
- |
- |
Predicted Value, A200 |
| - |
- |
Elongation of 20.1 % |
- |
- |
- |
Predicted Value, A80 Transverse |
| - |
- |
Elongation of 20.9 % |
- |
- |
- |
Predicted Value, A5 |
| - |
- |
Elongation of 22.7 % |
- |
- |
- |
Predicted Value, A50 |
| - |
- |
Elongation of 23.7 % |
- |
- |
- |
Predicted Value, Transverse |
| - |
20 °C |
Elongation of 22 % |
normalized or normalized formed (+N) |
EN 10149-3 |
Flat |
A80 |
| - |
20 °C |
Elongation of 27 % |
normalized or normalized formed (+N) |
EN 10149-3 |
Flat |
- |
| Hardness, Brinell |
- |
Hardness, Brinell of 241 [-] |
- |
- |
- |
Predicted Value, Transverse |
| Poisson's ratio |
- |
Poisson's ratio of 0.29 [-] |
- |
- |
- |
Typical for Low Carbon Steel |
| Reduction of area |
- |
Reduction of area of 40.3 % |
- |
- |
- |
Predicted Value |
| - |
- |
Reduction of area of 44.6 % |
- |
- |
- |
Predicted Value, Transverse |
| Shear modulus |
- |
Shear modulus of 82 GPa |
- |
- |
- |
Typical for Low Carbon Steel |
| Shear strength |
- |
Shear strength of 532.3 MPa |
- |
- |
- |
Predicted Value |
| Tensile strength |
20 °C |
Tensile strength of 430 - 550 MPa |
normalized or normalized formed (+N) |
EN 10149-3 |
Flat |
- |
| Yield strength |
- |
Yield strength of 252.2 MPa |
- |
- |
- |
Predicted Value, RP1 |
| - |
- |
Yield strength of 316 MPa |
- |
- |
- |
Predicted Value, RP1 Transverse |
| - |
- |
Yield strength of 325.8 MPa |
- |
- |
- |
Predicted Value, RP02 |
| - |
- |
Yield strength of 343.8 MPa |
- |
- |
- |
Predicted Value, Transverse |
| - |
- |
Yield strength of 410.2 MPa |
- |
- |
- |
Predicted Value, RP05 |
| - |
- |
Yield strength of 485.4 MPa |
- |
- |
- |
Predicted Value, RP02 Transverse |
| - |
- |
Yield strength of 489.8 MPa |
- |
- |
- |
Predicted Value, RP002 |
| - |
20 °C |
Yield strength of 315 MPa |
normalized or normalized formed (+N) |
EN 10149-3 |
Flat |
- |
Let our high-quality steel be the cornerstone of your architectural masterpieces and engineering marvels.