EN 10149-2 Grade S650MC thermomechanically rolled
EN 10149-2 Grade S650MC thermomechanically rolled introduction
The thermomechanical rolled steel is used for cold formed components like vehicle frames, axles and special sections.
Equivalent material: IS FeE650, DIN 1.8976, EN 1.8976, DIN S650MC, DIN QStE 650 TM
EN 10149-2 Grade S650MC thermomechanically rolled general
| Property | Value | Comment |
|---|---|---|
| Density | Density of 7.8 g/cm³ | Typical for Steel |
EN 10149-2 Grade S650MC thermomechanically rolled thermal
| Property | Value | Comment |
|---|---|---|
| Coefficient of thermal expansion | Coefficient of thermal expansion of 11.96 1/K | Predicted Value |
| Specific heat capacity | Specific heat capacity of 453.9 J/(kg·K) | Predicted Value |
| Thermal conductivity | Thermal conductivity of 37.64 W/(m·K) | Predicted Value |
EN 10149-2 Grade S650MC thermomechanically rolled chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Aluminium | Aluminium of 0.015 % | thermomechanically rolled | EN 10149-2 | Flat |
| Boron | Boron of 0.005 % | thermomechanically rolled | EN 10149-2 | Flat |
| Carbon | Carbon of 0.12 % | thermomechanically rolled | EN 10149-2 | Flat |
| Manganese | Manganese of 2 % | thermomechanically rolled | EN 10149-2 | Flat |
| Molybdenum | Molybdenum of 0.5 % | thermomechanically rolled | EN 10149-2 | Flat |
| Niobium | Niobium of 0.09 % | thermomechanically rolled | EN 10149-2 | Flat |
| Phosphorus | Phosphorus of 0.025 % | thermomechanically rolled | EN 10149-2 | Flat |
| Silicon | Silicon of 0.6 % | thermomechanically rolled | EN 10149-2 | Flat |
| Sulfur | Sulfur of 0.015 % | thermomechanically rolled | EN 10149-2 | Flat |
| Titanium | Titanium of 0.22 % | thermomechanically rolled | EN 10149-2 | Flat |
| Vanadium | Vanadium of 0.2 % | thermomechanically rolled | EN 10149-2 | Flat |
EN 10149-2 Grade S650MC thermomechanically rolled electrical
| Property | Value | Comment |
|---|---|---|
| Electrical conductivity | Electrical conductivity of 7 S/m | Predicted Value |
| Electrical resistivity | Electrical resistivity of 34 Ω·m | Predicted Value |
EN 10149-2 Grade S650MC thermomechanically rolled mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | - | Elastic modulus of 190 - 210 GPa | - | - | - | Typical for Steel |
| Elongation | - | Elongation of 13.0 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 13.2 % | - | - | - | Predicted Value, Transverse |
| - | - | Elongation of 17.5 % | - | - | - | Predicted Value, A50 |
| - | - | Elongation of 17.5 % | - | - | - | Predicted Value, A80 Transverse |
| - | - | Elongation of 18.3 % | - | - | - | Predicted Value, A5 |
| - | 20 °C | Elongation of 10 % | thermomechanically rolled | EN 10149-2 | Flat | A80 |
| - | 20 °C | Elongation of 10 % | thermomechanically rolled | EN 10149-2 | Flat | - |
| - | 20 °C | Elongation of 12 % | thermomechanically rolled | EN 10149-2 | Flat | A80 |
| - | 20 °C | Elongation of 12 % | thermomechanically rolled | EN 10149-2 | Flat | - |
| Hardness, Brinell | - | Hardness, Brinell of 248 [-] | - | - | - | Predicted Value, Transverse |
| Poisson's ratio | - | Poisson's ratio of 0.3 [-] | - | - | - | Typical for Steel |
| Reduction of area | - | Reduction of area of 38.9 % | - | - | - | Predicted Value |
| - | - | Reduction of area of 44.1 % | - | - | - | Predicted Value, Transverse |
| Shear modulus | - | Shear modulus of 80.1 GPa | - | - | - | Predicted Value |
| Shear strength | - | Shear strength of 583.8 MPa | - | - | - | Predicted Value |
| Tensile strength | 20 °C | Tensile strength of 700 - 880 MPa | thermomechanically rolled | EN 10149-2 | Flat | - |
| Yield strength | - | Yield strength of 293.5 MPa | - | - | - | Predicted Value, RP1 |
| - | - | Yield strength of 328.8 MPa | - | - | - | Predicted Value, RP1 Transverse |
| - | - | Yield strength of 505.4 MPa | - | - | - | Predicted Value, RP02 Transverse |
| - | - | Yield strength of 525.6 MPa | - | - | - | Predicted Value, Transverse |
| - | - | Yield strength of 547.5 MPa | - | - | - | Predicted Value, RP05 |
| - | - | Yield strength of 562.8 MPa | - | - | - | Predicted Value, RP02 |
| - | - | Yield strength of 623.6 MPa | - | - | - | Predicted Value, RP002 |
| - | 20 °C | Yield strength of 650 MPa | thermomechanically rolled | EN 10149-2 | Flat | - |