EN 10106 Grade M700-65A
EN 10106 Grade M700-65A introduction
Non-oriented fully processed electrical steel have guaranteed magnetic properties, in accordance with (or exceeding the levels required by) EN 10106:2015. As well as the maximum loss and minimum polarisation levels cited, full magnetic characterisation curves regarding losses, polarisation, permeability and apparent power at different frequencies are available on request.
This standard grade is available so that a steel grade can be selected according to the specific requirements of each application, from low alloy grades offering the advantage of excellent magnetic permeability, thermal conductivity and punchability to alloyed grades offering the advantage of very low losses, even at higher frequencies. A wide range of coatings is available, allowing further enhancement of punchability, reduction of interlaminar losses and improvement of corrosion protection.
Equivalent material: IEC M700-65A5
EN 10106 Grade M700-65A general
| Property |
Value |
Comment |
| Density |
Density of 7.75 g/cm³ |
for thickness 0.65 mm |
EN 10106 Grade M700-65A thermal
| Property |
Value |
Frequency |
Comment |
| Anisotropy of loss |
Anisotropy of loss of 10 % |
- |
(+/-) for thickness 0.65 mm | Guaranteed |
| Guaranteed polarization |
Guaranteed polarization of 1.57 [-] |
- |
min. | for thickness 0.65 mm | at 2500 A/m |
| - |
Guaranteed polarization of 1.67 [-] |
- |
min. | for thickness 0.65 mm | at 5000 A/m |
| - |
Guaranteed polarization of 1.76 [-] |
- |
min. | for thickness 0.65 mm | at 10000 A/m |
| Stacking factor |
Stacking factor of 0.97 mm |
- |
min. | for thickness 0.65 mm | Guaranteed |
| Typical core loss |
Typical core loss of 3 W/kg |
50Hz |
max. for thickness 0.65 mm | at 1 T |
| - |
Typical core loss of 8.98 W/kg |
60Hz |
max. for thickness 0.65 mm | at 1.5 T |
EN 10106 Grade M700-65A electrical
| Property |
- |
- |
| Application areas |
| Coating |
| Other |
| Min width |
Max width |
Min width |
Max width |
Min width |
Max width |
Min width |
Max width |
| M700-65A |
2 & 3 |
1030 |
1250 |
600 |
1220 |
20 |
600 |
400 |
1100 |
|
EN 10106 Grade M700-65A mechanical
| Property |
Value |
Comment |
| Elongation |
Elongation of 30 - 40 % |
for thickness 0.65 mm | Transverse | A80 |
| Hardness, Vickers |
Hardness, Vickers of 130 - 160 [-] |
for thickness 0.65 mm |
| Number of bends |
Number of bends of 10 [-] |
min. for thickness 0.65 mm | Guaranteed |
| Tensile strength |
Tensile strength of 420 - 470 MPa |
for thickness 0.65 mm | Transverse |
| Yield strength |
Yield strength of 280 - 330 MPa |
for thickness 0.65 mm | Transverse |
| Yield to strength ratio |
Yield to strength ratio of 0.67 - 0.72 [-] |
for thickness 0.65 mm |