EN 10095 Grade X6NiCrSiNCe35-25 solution annealed (+AT)
EN 10095 Grade X6NiCrSiNCe35-25 solution annealed (+AT) introduction
Steel X6NiCrSiNCe35-25 shows a highest application temperature of up to 1170 °C in air.
Equivalent material: ISO X6NiCrSiNCe35-25, GOST X6NiCrSiNCe35-25, ASTM A240UNSS35315, ASTM A480UNSS35315, UNS S35315, DIN 1.4854, DIN X6NiCrSiNCe35-25, AISI S35315, SAE S35315, EN 1.4854, ASTM S35315
EN 10095 Grade X6NiCrSiNCe35-25 solution annealed (+AT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.9 g/cm³ |
EN 10095 Grade X6NiCrSiNCe35-25 solution annealed (+AT) thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
200.0 °C |
Coefficient of thermal expansion of 1.55E-5 1/K |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.65E-5 1/K |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
| - |
800.0 °C |
Coefficient of thermal expansion of 1.75E-5 1/K |
| - |
1000.0 °C |
Coefficient of thermal expansion of 1.8E-5 1/K |
| Max service temperature, long |
- |
Max service temperature, long of 0 - 1170 °C |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 450 J/(kg·K) |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 11 W/(m·K) |
| - |
500.0 °C |
Thermal conductivity of 18.5 W/(m·K) |
EN 10095 Grade X6NiCrSiNCe35-25 solution annealed (+AT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.04 - 0.08 % |
| Cerium |
Cerium of 0.03 - 0.08 % |
| Chromium |
Chromium of 24 - 26 % |
| Manganese |
Manganese of 2 % |
| Nickel |
Nickel of 34 - 36 % |
| Nitrogen |
Nitrogen of 0.12 - 0.2 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1.2 - 2 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10095 Grade X6NiCrSiNCe35-25 solution annealed (+AT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1E-6 Ω·m |
EN 10095 Grade X6NiCrSiNCe35-25 solution annealed (+AT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
Typical for Steel |
| Elongation |
20.0 °C |
Elongation of 40 % |
- |
| Elongation A80 |
20.0 °C |
Elongation A80 of 40 % |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 210 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 650 - 850 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 300 MPa |
- |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 340 MPa |
- |