EN 10095 Grade X6CrNiSiNCe19-10 solution annealed (+AT)
EN 10095 Grade X6CrNiSiNCe19-10 solution annealed (+AT) introduction
Steel X6CrNiSiNCe19-10 shows a highest application temperature of up to 1050 °C in air.
Equivalent material: GB 05Cr19Ni10Si2CeN, GB S30450, ISO X6CrNiSiNCe19-10, GOST X6CrNiSiNCe19-10, ASTM A480UNSS30415, UNS S30415, DIN 1.4818, AISI S30415, SAE S30415, EN 1.4818, ASTM S30415
EN 10095 Grade X6CrNiSiNCe19-10 solution annealed (+AT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.8 g/cm³ |
EN 10095 Grade X6CrNiSiNCe19-10 solution annealed (+AT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
200.0 °C |
Coefficient of thermal expansion of 1.65E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.8E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.85E-5 1/K |
- |
| - |
800.0 °C |
Coefficient of thermal expansion of 1.9E-5 1/K |
- |
| - |
1000.0 °C |
Coefficient of thermal expansion of 2E-5 1/K |
- |
| Max service temperature, long |
- |
Max service temperature, long of 0 - 1050 °C |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 21 W/(m·K) |
- |
EN 10095 Grade X6CrNiSiNCe19-10 solution annealed (+AT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.04 - 0.08 % |
| Cerium |
Cerium of 0.03 - 0.08 % |
| Chromium |
Chromium of 18 - 20 % |
| Manganese |
Manganese of 1 % |
| Nickel |
Nickel of 9 - 11 % |
| Nitrogen |
Nitrogen of 0.12 - 0.2 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 - 2 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10095 Grade X6CrNiSiNCe19-10 solution annealed (+AT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
EN 10095 Grade X6CrNiSiNCe19-10 solution annealed (+AT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation |
20.0 °C |
Elongation of 40 % |
- |
| Elongation A80 |
20.0 °C |
Elongation A80 of 30 % |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 210 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 600 - 800 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 290 MPa |
- |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 330 MPa |
- |
Experience the power of our premium steel, forged to perfection for exceptional performance.