EN 10095 Grade X25CrMnNiN25-9-7 solution annealed (+AT)
EN 10095 Grade X25CrMnNiN25-9-7 solution annealed (+AT) introduction
Steel X25CrMnNiN25-9-7 shows a highest application temperature of up to 1150 °C in air.
Equivalent material: DIN 1.4872, EN 1.4872
EN 10095 Grade X25CrMnNiN25-9-7 solution annealed (+AT) general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.8 g/cm³ |
EN 10095 Grade X25CrMnNiN25-9-7 solution annealed (+AT) thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 200.0 °C | Coefficient of thermal expansion of 1.65E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.8E-5 1/K | - |
| - | 600.0 °C | Coefficient of thermal expansion of 1.85E-5 1/K | - |
| - | 800.0 °C | Coefficient of thermal expansion of 1.9E-5 1/K | - |
| - | 1000.0 °C | Coefficient of thermal expansion of 1.95E-5 1/K | - |
| Max service temperature, long | - | Max service temperature, long of 0 - 1150 °C | - |
| Melting point | - | Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel |
| Specific heat capacity | 20.0 °C | Specific heat capacity of 500 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 14.5 W/(m·K) | - |
| - | 500.0 °C | Thermal conductivity of 20 W/(m·K) | - |
EN 10095 Grade X25CrMnNiN25-9-7 solution annealed (+AT) chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.2 - 0.3 % |
| Chromium | Chromium of 24 - 26 % |
| Manganese | Manganese of 8 - 10 % |
| Nickel | Nickel of 6 - 8 % |
| Nitrogen | Nitrogen of 0.2 - 0.4 % |
| Phosphorus | Phosphorus of 0.05 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.015 % |
EN 10095 Grade X25CrMnNiN25-9-7 solution annealed (+AT) electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 7.5E-7 Ω·m |
EN 10095 Grade X25CrMnNiN25-9-7 solution annealed (+AT) mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 195 GPa | Typical for Austenitic Stainless Steel |
| Elongation | 20.0 °C | Elongation of 25 % | - |
| Hardness, Brinell | 20.0 °C | Hardness, Brinell of 311 [-] | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Austenitic Stainless Steel |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Austenitic Stainless Steel |
| Tensile strength | 20.0 °C | Tensile strength of 850 - 1050 MPa | - |
| Yield strength Rp0.2 | 20.0 °C | Yield strength Rp0.2 of 500 MPa | - |
| Yield strength Rp1.0 | 20.0 °C | Yield strength Rp1.0 of 540 MPa | - |