EN 10095 Grade X10NiCrSiNb35-22 solution annealed (+AT)
EN 10095 Grade X10NiCrSiNb35-22 solution annealed (+AT) introduction
Steel X10NiCrSiNb35-22 shows a highest application temperature of up to 1100 °C in air.
Equivalent material: DIN 1.4887, EN 1.4887
EN 10095 Grade X10NiCrSiNb35-22 solution annealed (+AT) general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 8 g/cm³ |
EN 10095 Grade X10NiCrSiNb35-22 solution annealed (+AT) thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 200.0 °C | Coefficient of thermal expansion of 1.55E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.6E-5 1/K | - |
| - | 600.0 °C | Coefficient of thermal expansion of 1.7E-5 1/K | - |
| - | 800.0 °C | Coefficient of thermal expansion of 1.77E-5 1/K | - |
| - | 1000.0 °C | Coefficient of thermal expansion of 1.8E-5 1/K | - |
| Max service temperature | - | Max service temperature of 300 °C | Typical for Duplex Stainless Steel |
| Max service temperature, long | - | Max service temperature, long of 0 - 1100 °C | - |
| Melting point | - | Melting point of 1375 - 1450 °C | Typical for Duplex Stainless Steel |
| Specific heat capacity | 20.0 °C | Specific heat capacity of 460 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 12 W/(m·K) | - |
| - | 500.0 °C | Thermal conductivity of 19.5 W/(m·K) | - |
EN 10095 Grade X10NiCrSiNb35-22 solution annealed (+AT) chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.15 % |
| Chromium | Chromium of 20 - 23 % |
| Manganese | Manganese of 2 % |
| Nickel | Nickel of 33 - 37 % |
| Niobium | Niobium of 1 - 1.5 % |
| Nitrogen | Nitrogen of 0.11 % |
| Phosphorus | Phosphorus of 0.03 % |
| Silicon | Silicon of 1 - 2 % |
| Sulfur | Sulfur of 0.015 % |
EN 10095 Grade X10NiCrSiNb35-22 solution annealed (+AT) electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 1E-6 Ω·m |
EN 10095 Grade X10NiCrSiNb35-22 solution annealed (+AT) mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 200 GPa | Typical for Duplex Stainless Steel |
| Elongation | 20.0 °C | Elongation of 40 % | - |
| Hardness, Brinell | 20.0 °C | Hardness, Brinell of 200 [-] | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Duplex Stainless Steel |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Duplex Stainless Steel |
| Tensile strength | 20.0 °C | Tensile strength of 500 - 650 MPa | - |
| Yield strength Rp0.2 | 20.0 °C | Yield strength Rp0.2 of 270 MPa | - |
| Yield strength Rp1.0 | 20.0 °C | Yield strength Rp1.0 of 300 MPa | - |