EN 10089 Grade 60SiCrV7 quenched and tempered (+QT)
EN 10089 Grade 60SiCrV7 quenched and tempered (+QT) introduction
The steel 60SiCrV7 is used for hot formed springs, like leaf springs > 7 mm thickness for the vehicle construction as well as for coil springs and diaphragm springs also for the mechanical engineering.
Equivalent material: DIN 1.8153, DIN 60SiCrV7, EN 1.8153
EN 10089 Grade 60SiCrV7 quenched and tempered (+QT) general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 g/cm³ | Typical for Steel |
EN 10089 Grade 60SiCrV7 quenched and tempered (+QT) chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.56 - 0.64 % |
| Chromium | Chromium of 0.2 - 0.4 % |
| Manganese | Manganese of 0.7 - 1 % |
| Phosphorus | Phosphorus of 0.03 % |
| Silicon | Silicon of 1.5 - 2 % |
| Sulfur | Sulfur of 0.025 % |
| Vanadium | Vanadium of 0.1 - 0.2 % |
EN 10089 Grade 60SiCrV7 quenched and tempered (+QT) mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 190 - 210 GPa | Typical for Steel |
| Elongation | 20.0 °C | Elongation of 5 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Steel |
| Reduction of area | 20.0 °C | Reduction of area of 30 % | - |
| Tensile strength | 20.0 °C | Tensile strength of 1700 - 2000 MPa | - |
| Yield strength Rp0.2 | 20.0 °C | Yield strength Rp0.2 of 1650 MPa | - |