EN 10089 Grade 50SiCrMo6 quenched and tempered (+QT)
EN 10089 Grade 50SiCrMo6 quenched and tempered (+QT) introduction
The steel 50SiCrMo6 is used for hot formed springs for high stress in the vehicle engineering.
Equivalent material: DIN 1.8063, DIN 50SiCrMo6, EN 1.8063
EN 10089 Grade 50SiCrMo6 quenched and tempered (+QT) general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 g/cm³ | Typical for Steel |
EN 10089 Grade 50SiCrMo6 quenched and tempered (+QT) chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.46 - 0.54 % |
| Chromium | Chromium of 0.8 - 1.1 % |
| Manganese | Manganese of 0.7 - 1 % |
| Molybdenum | Molybdenum of 0.2 - 0.35 % |
| Phosphorus | Phosphorus of 0.03 % |
| Silicon | Silicon of 1.4 - 1.8 % |
| Sulfur | Sulfur of 0.025 % |
EN 10089 Grade 50SiCrMo6 quenched and tempered (+QT) mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 190 - 210 GPa | Typical for Steel |
| Elongation | 20.0 °C | Elongation of 6 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Steel |
| Reduction of area | 20.0 °C | Reduction of area of 30 % | - |
| Tensile strength | 20.0 °C | Tensile strength of 1650 - 1950 MPa | - |
| Yield strength Rp0.2 | 20.0 °C | Yield strength Rp0.2 of 1420 MPa | - |