EN 10088-1 Grade X3CrNiMo13-4 quenched and tempered (+QT650)
EN 10088-1 Grade X3CrNiMo13-4 quenched and tempered (+QT650) introduction
Molybdenum alloyed martensitic-austenitic (nickel martensitic) corrosion resisting steel.
Equivalent material: GB 04Cr13Ni5Mo, GB S41595, ISO X3CrNiMo13-4, ISO 4313-415-00-I, ISO MM14A, UNS S41500, ASTM A276UNSS41500, ASTM A480UNSS41500, DIN X5CrNi13-4, DIN X3CrNiMo13-4, DIN 1.4313, DIN G-X5CrNi13-4, DIN X4CrNi13-4, AFNOR Z6CN13-04, BS 425C11, AISI 415, AISI S41500, SAE 415, SAE S41500, JIS SUSF6NM, JIS SCS5, JIS SCS6, EN GX5CrNi134, EN 1.4313, ASTM CA6NM, ASTM F6NM, UNS J91540, UNS S42400
EN 10088-1 Grade X3CrNiMo13-4 quenched and tempered (+QT650) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.58 - 7.7 g/cm³ |
EN 10088-1 Grade X3CrNiMo13-4 quenched and tempered (+QT650) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.02E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.09E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.13E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.16E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.22E-5 1/K |
- |
| - |
700.0 °C |
Coefficient of thermal expansion of 1.24E-5 1/K |
- |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 430 - 439 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 474 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 492 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 538 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 564 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 598 J/(kg·K) |
- |
| - |
700.0 °C |
Specific heat capacity of 647 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 15.7 - 25 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 17.1 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 18.6 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 20 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 21.2 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 22.3 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 23.1 W/(m·K) |
- |
| - |
700.0 °C |
Thermal conductivity of 23.8 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 4.7 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 4.5 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 4.6 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 4.7 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 4.5 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 4.3 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 3.7 mm²/s |
- |
| - |
700.0 °C |
Thermal diffusivity of 3 mm²/s |
- |
EN 10088-1 Grade X3CrNiMo13-4 quenched and tempered (+QT650) chemical
| Property |
Value |
| Carbon |
Carbon of 0.05 % |
| Chromium |
Chromium of 12 - 14 % |
| Manganese |
Manganese of 1.5 % |
| Molybdenum |
Molybdenum of 0.3 - 0.7 % |
| Nickel |
Nickel of 3.5 - 4.5 % |
| Nitrogen |
Nitrogen of 0.02 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.7 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10088-1 Grade X3CrNiMo13-4 quenched and tempered (+QT650) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 6E-7 - 9.19E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 9.48E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 9.87E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 1.03E-6 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 1.07E-6 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 1.12E-6 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 1.18E-6 Ω·m |
| - |
700.0 °C |
Electrical resistivity of 1.24E-6 Ω·m |
EN 10088-1 Grade X3CrNiMo13-4 quenched and tempered (+QT650) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 - 218 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 195 - 213 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 185 - 206 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 175 - 198 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 170 - 190 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 180 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 167 GPa |
- |
| - |
700.0 °C |
Elastic modulus of 150 GPa |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Yield strength Rp0.2 |
100.0 °C |
Yield strength Rp0.2 of 500 MPa |
- |
| - |
150.0 °C |
Yield strength Rp0.2 of 490 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 480 MPa |
- |
| - |
250.0 °C |
Yield strength Rp0.2 of 480 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 460 MPa |
- |
| - |
350.0 °C |
Yield strength Rp0.2 of 450 MPa |
- |