EN 10088-1 Grade X12CrMnNiN17-7-5 strain-hardened (+C1000)
EN 10088-1 Grade X12CrMnNiN17-7-5 strain-hardened (+C1000) introduction
The austenitic material X12CrMnNiN17-7-5 is used in solution annealed condition in the form of cold rolled strip, warm rolled strip and warm rolled sheet. It is resistant to intercrystalline corrosion in delivery condition not in sensitized condition.
Equivalent material: ISO X12CrMnNiN17-7-5, GB 12Cr17Mn6Ni5N, GB S35350, IS 201, IS X10Cr17Mn6Ni4N20, ISO 4372-201-00-I, ISO AP29O, JIS SUS201, KS STS201, ASTM A240Type201, ASTM A276Type201, ASTM A480Type201, ASTM A666Type201, ASTM A959UNSS20100, SAE 20201, AISI 201, UNS S20100, DIN 1.4372, DIN X12CrMnNiN17-7-5, SAE 201, EN 1.4372, ISO 13, ASTM TP201, ASTM 201-1, ASTM 201-2
EN 10088-1 Grade X12CrMnNiN17-7-5 strain-hardened (+C1000) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.8 g/cm³ |
EN 10088-1 Grade X12CrMnNiN17-7-5 strain-hardened (+C1000) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
EN 10088-1 Grade X12CrMnNiN17-7-5 strain-hardened (+C1000) chemical
| Property |
Value |
| Carbon |
Carbon of 0.15 % |
| Chromium |
Chromium of 16 - 18 % |
| Manganese |
Manganese of 5.5 - 7.5 % |
| Nickel |
Nickel of 3.5 - 5.5 % |
| Nitrogen |
Nitrogen of 0.05 - 0.25 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10088-1 Grade X12CrMnNiN17-7-5 strain-hardened (+C1000) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7E-7 Ω·m |
EN 10088-1 Grade X12CrMnNiN17-7-5 strain-hardened (+C1000) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 194 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 186 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 179 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 172 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 165 GPa |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 1000 - 1150 MPa |
- |