EN 10088-1 Grade X105CrMo17 soft annealed (+A)
EN 10088-1 Grade X105CrMo17 soft annealed (+A) introduction
Material X105CrMo17 is comparable to X 105 CrMo 17 acc. to SEW 400 :1991-02. The material is a high hardenable and wear resistant steel. It is particularly suitable for small ball bearings, for cutting tools, such as butchers knives, scalpels, for valve needles and spray nozzles. Despite the higher Cr-content the corrosion resistance is owing to the high C-content comparable to 13 per cent Cr-steels.
Equivalent material: AISI 440C, AS 440C, GB 11Cr17, AFNOR Z100CD17, GOST 110Ch18M-SChD, GB S44091, ISO X105CrMo17, JIS SUS440C, KS STS440C, MSZ KO14, UNS S44004, AMS S44004, ASTM 440C, ASTM S44004, SAE 51440C, SAE 440C, GB 102Cr17Mo, GB S45990, IS 440, IS X108Cr17Mo, ISO X110Cr17, GOST 110Х18M-СХД, ASTM A276Type440C, ASTM A314Type440C, ASTM A473Type440C, AISI Type440C, DIN 1.4125, DIN X105CrMo17, UNI X 105CrMo17, EN 1.4125, GOST 95Ch18, GB 108Cr17, AMS 5618
EN 10088-1 Grade X105CrMo17 soft annealed (+A) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.56 - 7.7 g/cm³ |
EN 10088-1 Grade X105CrMo17 soft annealed (+A) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 9.9E-6 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.03E-5 - 1.04E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.12E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.16E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
- |
| - |
700.0 °C |
Coefficient of thermal expansion of 1.24E-5 1/K |
- |
| - |
800.0 °C |
Coefficient of thermal expansion of 1.29E-5 1/K |
- |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 430 - 450 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 482 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 506 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 525 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 547 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 576 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 616 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 15 - 16 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 17.2 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 18.6 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 20 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 21.2 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 22.3 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 23.3 W/(m·K) |
- |
| - |
700.0 °C |
Thermal conductivity of 24.1 W/(m·K) |
- |
| - |
800.0 °C |
Thermal conductivity of 25.5 W/(m·K) |
- |
| - |
900.0 °C |
Thermal conductivity of 26.9 W/(m·K) |
- |
| - |
1000.0 °C |
Thermal conductivity of 28.3 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 4.7 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 4.5 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 4.5 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 4.6 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 4.4 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 4.1 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 3.6 mm²/s |
- |
EN 10088-1 Grade X105CrMo17 soft annealed (+A) chemical
| Property |
Value |
| Carbon |
Carbon of 0.95 - 1.2 % |
| Chromium |
Chromium of 16 - 18 % |
| Manganese |
Manganese of 1 % |
| Molybdenum |
Molybdenum of 0.4 - 0.8 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10088-1 Grade X105CrMo17 soft annealed (+A) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 8E-7 - 9.06E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 9.42E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 9.87E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 1.03E-6 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 1.08E-6 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 1.12E-6 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 1.18E-6 Ω·m |
| - |
700.0 °C |
Electrical resistivity of 1.22E-6 Ω·m |
| - |
800.0 °C |
Electrical resistivity of 1.24E-6 Ω·m |
| - |
900.0 °C |
Electrical resistivity of 1.26E-6 Ω·m |
| - |
1000.0 °C |
Electrical resistivity of 1.27E-6 Ω·m |
EN 10088-1 Grade X105CrMo17 soft annealed (+A) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 215 - 218 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 212 - 213 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 205 - 206 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 198 - 200 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 190 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 180 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 167 GPa |
- |
| - |
700.0 °C |
Elastic modulus of 150 GPa |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 285 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |