EN 10084 Grade 17NiCrMo6-4 quenched (+Q)
EN 10084 Grade 17NiCrMo6-4 quenched (+Q) introduction
The case-hardening steel is used for high loaded gear parts.
Equivalent material: EN 1.6566, IS 15Ni5Cr4Mo1(-S), ISO 17NiCrMo6-4, DIN 1.6566, DIN 17NiCrMo6-4
EN 10084 Grade 17NiCrMo6-4 quenched (+Q) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Nickel Chromium Molybdenum Steel |
EN 10084 Grade 17NiCrMo6-4 quenched (+Q) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.3E-5 1/K |
Typical for Nickel Chromium Molybdenum Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Nickel Chromium Molybdenum Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 448 - 670 J/(kg·K) |
Typical for Nickel Chromium Molybdenum Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 34 - 54 W/(m·K) |
Typical for Nickel Chromium Molybdenum Steel |
EN 10084 Grade 17NiCrMo6-4 quenched (+Q) chemical
| Property |
Value |
| Carbon |
Carbon of 0.14 - 0.2 % |
| Chromium |
Chromium of 0.8 - 1.1 % |
| Copper |
Copper of 0.4 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Molybdenum |
Molybdenum of 0.15 - 0.25 % |
| Nickel |
Nickel of 1.2 - 1.5 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10084 Grade 17NiCrMo6-4 quenched (+Q) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Nickel Chromium Molybdenum Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Nickel Chromium Molybdenum Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 800 - 1200 MPa |
- |