EN 10083-3 Grade 38MnB5 quenched and tempered (+QT)
EN 10083-3 Grade 38MnB5 quenched and tempered (+QT) introduction
Boron-alloyed tempering steel for general machine engineering.
The steel is shearable in the non treated condition.
Equivalent material: GB 40MnBH, GB 40MnBAH, GB A71405, GB A71407, ISO 39MnB5, GOST 40GR, GOST 40ГP, DIN 1.5532, DIN 38MnB5, JIS SWRCHB737, EN 1.5532, ISO 38MnB5
EN 10083-3 Grade 38MnB5 quenched and tempered (+QT) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Medium Carbon Steel |
EN 10083-3 Grade 38MnB5 quenched and tempered (+QT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
Typical for Medium Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1380 - 1514 °C |
Typical for Medium Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 470 - 520 J/(kg·K) |
Typical for Medium Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 21 - 52 W/(m·K) |
Typical for Medium Carbon Steel |
EN 10083-3 Grade 38MnB5 quenched and tempered (+QT) chemical
| Property |
Value |
| Boron |
Boron of 1E-3 - 5E-3 % |
| Carbon |
Carbon of 0.36 - 0.42 % |
| Manganese |
Manganese of 1.15 - 1.45 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10083-3 Grade 38MnB5 quenched and tempered (+QT) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10083-3 Grade 38MnB5 quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Medium Carbon Steel |
| Elongation |
20.0 °C |
Elongation of 12 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Medium Carbon Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 50 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 850 - 1250 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 700 - 900 MPa |
- |