EN 10028-7 Grade X6CrNiTi12 soft annealed (+A)
EN 10028-7 Grade X6CrNiTi12 soft annealed (+A) introduction
The ferritic steel X6CrNiTi12 is used in the annealed condition for cold rolled strip as well as for hot rolled strip and sheet.
Equivalent material: ISO X6CrNiTi12, ASTM A240UNSS40975, UNS S40975, DIN 1.4516, AISI S40975, SAE S40975, EN 1.4516, ASTM S40975
EN 10028-7 Grade X6CrNiTi12 soft annealed (+A) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.7 g/cm³ |
EN 10028-7 Grade X6CrNiTi12 soft annealed (+A) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.15E-5 1/K |
- |
| Melting point |
- |
Melting point of 1425 - 1530 °C |
Typical for Ferritic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 30 W/(m·K) |
- |
EN 10028-7 Grade X6CrNiTi12 soft annealed (+A) chemical
| Property |
Value |
| Carbon |
Carbon of 0.08 % |
| Chromium |
Chromium of 10.5 - 12.5 % |
| Manganese |
Manganese of 1.5 % |
| Nickel |
Nickel of 0.5 - 1.5 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.7 % |
| Sulfur |
Sulfur of 0.015 % |
| Titanium |
Titanium of 0.05 - 0.35 % |
EN 10028-7 Grade X6CrNiTi12 soft annealed (+A) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 6E-7 Ω·m |
EN 10028-7 Grade X6CrNiTi12 soft annealed (+A) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 220 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 215 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 210 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 205 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 195 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 20 - 23 % |
- |
| Elongation A80 |
20.0 °C |
Elongation A80 of 20 - 23 % |
- |
| Elongation A80, transverse |
20.0 °C |
Elongation A80, transverse of 20 - 23 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 20 - 23 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Ferritic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Ferritic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 450 - 650 MPa |
- |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 450 - 650 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 250 - 320 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 300 MPa |
- |
| - |
150.0 °C |
Yield strength Rp0.2 of 270 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 250 MPa |
- |
| - |
250.0 °C |
Yield strength Rp0.2 of 245 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 225 MPa |
- |
| - |
350.0 °C |
Yield strength Rp0.2 of 215 MPa |
- |
| Yield strength Rp0.2, transverse |
20.0 °C |
Yield strength Rp0.2, transverse of 250 - 320 MPa |
- |